Published: 01 January 2005
Fig. 56 Secondary-tension test showing the geometries of holes and slots. L ≈ h ; w a ≥2 h ; b = h /4; D = h /2 More
Image
Published: 01 January 2005
Fig. 57 Results of secondary-tension test on aluminum alloy 7075. Source: Ref 71 More
Image
Published: 01 January 2005
Fig. 13 Secondary-tension test showing the geometries of holes and slots. L ≅ h ; w a ≅ 2 = h ; b = h /4; D = h /2 More
Image
Published: 01 January 2005
Fig. 14 Results of secondary-tension test on aluminum alloy 7075. Source: Ref 20 More
Series: ASM Handbook
Volume: 14A
Publisher: ASM International
Published: 01 January 2005
DOI: 10.31399/asm.hb.v14a.a0009007
EISBN: 978-1-62708-185-6
..., compression test, and bend test. It examines specialized tests including plane-strain compression test, partial-width indentation test, secondary-tension test, and ring compression test. The article explains that workability is determined by two main factors: the ability to deform without fracture...
Series: ASM Handbook
Volume: 14A
Publisher: ASM International
Published: 01 January 2005
DOI: 10.31399/asm.hb.v14a.a0004017
EISBN: 978-1-62708-185-6
... tests, such as the tension test, ring compression test, plane-strain compression test, bend test, indentation test, and forgeability test. It concludes with information on the role of the finite-element modeling software used in workability analysis. bend test bulk forming processes cracking...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000614
EISBN: 978-1-62708-181-8
... of transition from fibrous fracture in the central zone to fracture by shear in the surrounding lip. Visible in the lower portion of the fractograph are the equiaxed dimples (viewed obliquely) that are characteristic of fracture in pure tension; above are the elongated dimples of the shear lip. Note...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000612
EISBN: 978-1-62708-181-8
... A classic example of cup-and-cone tension-overload fracture in an unnotched specimen of 13-8 PH stainless steel with tensile strength of 1634 MPa (237 ksi) and 47% reduction of area. There are circumferential secondary cracks at the base of the shear lip. See also Fig. 721 . 9× Fig. 721 SEM view...
Series: ASM Handbook
Volume: 6A
Publisher: ASM International
Published: 31 October 2011
DOI: 10.31399/asm.hb.v06a.a0005594
EISBN: 978-1-62708-174-0
... as 0.4 mm (0.016 in.) apart. Fig. 14 Microhardness traverse across the weld, heat-affected zone, and unaffected base materials. (a) Schematic of a weld cross section. (b) Typical cross section Weld Integrity Two types of weld tension tests are typically done to assess the weld tensile...
Series: ASM Handbook
Volume: 1
Publisher: ASM International
Published: 01 January 1990
DOI: 10.31399/asm.hb.v01.a0001032
EISBN: 978-1-62708-161-0
... is that it uses a specimen of simple shape; another is that as-cast materials can be readily tested. One edge of the specimen can contain original surface defects. The test can be conducted hot or cold. Secondary-Tension Test The secondary-tension test is a modification of the partial-width indentation...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000613
EISBN: 978-1-62708-181-8
... fracture and revealing the equiaxed dimples expected in a tension-overload fracture. No secondary cracks are visible. SEM, 4000× Fig. 786 High-cycle fatigue fracture in AISI H11 tool steel heat treated to a tensile strength of 2041 MPa (296 ksi) and 48% reduction of area, which broke after...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000623
EISBN: 978-1-62708-181-8
... titanium alloys Fig. 1103, 1104, 1105, 1106, 1107, 1108, 1109, 1110 Fatigue crack growth fracture topography in a Ti-6Al-2Sn-4Zr-2Mo-0.1Si (Ti-6242, UNS R54620) forging, α + β processed prior to β heat treatment and aging. Compact tension specimen tested in air at 25 °C (75 °F). As crack growth rate...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000621
EISBN: 978-1-62708-181-8
..., tension-overload fracture surface, ductile fracture, cone-shaped fracture surface, intergranular crack propagation, transgranular crack propagation, stress-corrosion cracking, hydrogen damage, and grain-boundary separation of these alloys. Fractographs are also provided for a forged aircraft main-landing...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000619
EISBN: 978-1-62708-181-8
...) shows the necked-down profile of a tension fracture, ∼50× Fig. 919 Longitudinal section through a tension fracture in a warp wire of a Fourdrinier wire cloth of phosphor bronze C. Slip lines are visible throughout the microstructure. Plastic flow and reduction in area at the fracture (top...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000603
EISBN: 978-1-62708-181-8
... irons tested at room temperature and at −40 °C (−40 °F), respectively. SEM, ∼1900× (F.J. Worzala, University of Wisconsin) Fig. 62 Fig. 63 Fig. 64 Fig. 65, 66, 67 Slow monotonic (tension or bending) fracture characteristics of heat-treated ductile irons. Fig. 65 : Normalized...
Series: ASM Handbook
Volume: 21
Publisher: ASM International
Published: 01 January 2001
DOI: 10.31399/asm.hb.v21.a0003444
EISBN: 978-1-62708-195-5
.... For mechanically bolted joints, tests are recommended that characterize the joint for various failure modes: bearing, notched tension/compression, bearing/by-pass, shear-out, and fastener pull-through. Test matrices are provided in MIL-HDBK-17. A straightforward test method to determine material bearing strength...
Series: ASM Handbook
Volume: 12
Publisher: ASM International
Published: 01 January 1987
DOI: 10.31399/asm.hb.v12.a0000608
EISBN: 978-1-62708-181-8
... degree of pulsation in the applied stress during testing. TEM p-c replica, 6500× Fig. 392 Surface of a fracture in a notched specimen of AISI 4340 steel that was broken in tension overload, showing scattered dimples. It is not certain whether the remainder of the surface in this area consists...
Series: ASM Handbook
Volume: 14A
Publisher: ASM International
Published: 01 January 2005
DOI: 10.31399/asm.hb.v14a.a0009005
EISBN: 978-1-62708-185-6
... will be undertaken in the future to establish the path-depe