This article focuses on the modeling of microstructure evolution during thermomechanical processing in the two-phase field for alpha/beta and beta titanium alloys. It also discusses the mechanisms of spheroidization, the coarsening, particle growth, and phase decomposition in titanium alloys, with their corresponding equations.

Sintering provides the interparticle bonding that generates the attractive forces needed to hold together the otherwise loose ceramic powder mass. It also improves hardness, strength, transparency, toughness, electrical conductivity, thermal expansion, magnetic saturation, corrosion resistance, and other properties. This article discusses the fundamentals of sintering and its effects on pore structures and particle density. It addresses some of the more common sintering methods, including solid-state, liquid-phase, and gas pressure sintering, and presents alternative processes such as reaction sintering and self-propagating, high-temperature synthesis. It also describes several pressure densification methods, including hot isostatic pressing, gas pressure sintering, molten particle deposition, and sol-gel processing. The article concludes with a section on grain growth that discusses the underlying mechanisms and kinetics and the relationship between grain growth and densification.

This article describes the fatigue properties of particle-reinforced metal-matrix composites (PR-MMCs) in terms of mechanisms of crack initiation, fatigue life, and fatigue crack growth. It reviews specimen preparation and microscopic procedures that are used in fatigue testing of MMCs. It also describes the evaluation of the long fatigue crack growth behavior of MMCs by using the test methods and specimens that are used for unreinforced metallic alloys. Fractography of MMCs under plane-strain conditions is also described with information on the observed features of MMC fatigue fracture surfaces and their observation methods.

Sintering is a thermal treatment process in which a powder or a porous material, already formed into the required shape, is converted into a useful article with the requisite microstructure. Sintering can be classified as solid-state, viscous, liquid-phase, and pressure-assisted (or pressure) sintering. This article provides information on the mechanisms and theoretical analysis of sintering and focuses on the types, mechanisms, process and microstructural variables, computer simulation, stages, and fundamentals of densification and grain growth of solid-state sintering and liquid-phase sintering. It describes the models for viscous sintering and the methods used in pressure-assisted sintering, namely, uniaxial hot pressing, hot isostatic pressing, sinter forging, and spark plasma sintering.

Any model that describes the early stage of cavitation must therefore address experimental observations of continuous nucleation, cracklike interface cavities, cavity growth from nanometer-scale sizes, and debonding at particle interfaces and formation of large-faceted cavities. This article summarizes the microstructural details of the early stages of cavitation in metals for understanding the interface-constrained plasticity cavitation model. It discusses formulation, predictions and implications, involved in analysis of cavitation under constrained conditions.

This article focuses on the general internal state variable method, and its simplification, for single-parameter models, in which the microstructure evolution may be treated as an isokinetic reaction. It explains that isokinetic microstructure models are applied to diffusional transformations in fusion welding, covering particle dissolution, growth, and coarsening of precipitates in the heat-affected zone. The article discusses the versatility of the internal state variable approach in modeling of nonisothermal transformations for various materials and processes. It describes the process models applied to predict the microstructure evolution in Al-Mg-Si alloys during multistage thermal processing involving heat treatment and welding. The article also provides information on the microstructure models exploited in engineering design to optimize the load-bearing capacity of welded aluminum components.

Diffusion is the process by which molecules, atoms, ions, point defects, or other particle types migrate from a region of higher concentration to one of lower concentration. This article focuses on the diffusivity data and modeling of lattice diffusion in solid-state materials, presenting their diffusion equations. It discusses different methods for evaluating the diffusivity of a material, including the measurement of diffusion coefficients, composition profiles, and layer growth widths. The article reviews the various types of direct and indirect diffusion experiments to extract tracer, intrinsic, and chemical diffusivities. It provides information on the applications of single-phase and multiphase diffusion.

This article describes the changes in structure and properties that occur when cold worked metals and alloys are annealed. Recovery, recrystallization, and grain growth are the three stages of structural change that occur when cold-worked metal is annealed. The driving force and extent of structural or property changes may depend on alloy structure and the degree of prior work.

This article discusses selected highlights of thermodynamic relationships during solidification and nucleation kinetics behavior in connection with the basis of nucleation treatments, such as grain refinement and inoculation, to provide a summary of nucleation phenomena during casting. The article describes nucleation phenomenon such as homogeneous nucleation and heterogeneous nucleation. It examines various grain refinement models, such as the carbide-boride model, the free growth model, and the constitutional undercooling model. The article concludes with information on the thermal analysis techniques for assessing grain-refining characteristics during master alloy processing.

Recovery, recrystallization, and grain growth are microstructural changes that occur during annealing after cold plastic deformation and/or during hot working of metals. This article reviews the structure of the deformed state and describes the changes in the properties and microstructures of a cold-worked metal during recovery stage. It discusses the recrystallization that occurs by the nucleation and growth of grains. The article also reviews the growth behavior of the grains, explaining that the grain growth can be classified into two types: normal or continuous grain growth and abnormal or discontinuous grain growth. It also examines the key mechanisms that control microstructure evolution during hot working and subsequent heat treatment. These include dynamic recovery, dynamic recrystallization, metadynamic recrystallization, static recovery, static recrystallization, and grain growth.

Recovery, recrystallization, and grain growth are the stages that a cold worked metal undergoes when it is annealed. This article describes the changes in the structure and properties that occur on annealing a cold-worked metal. It summarizes the experimental recrystallization studies by Burke and Turnbull with six laws of recrystallization. Applications of these laws of recrystallization are discussed in detail with examples. The article reviews the classification of grain growth according to the growth behavior of grains, namely, normal or continuous grain growth and abnormal or discontinuous grain growth. The latter has also been termed exaggerated grain growth, coarsening, or secondary recrystallization.

This article begins with the one-component, or unary, diagram for magnesium. The diagram shows what phases are present as a function of the temperature and pressure. When two metals are mixed in the liquid state to produce a solution, the resulting alloy is called a binary alloy. The article describes the various types of solid solutions such as interstitial solid solutions and substitutional solid solutions. Free energy is important because it determines whether or not a phase transformation is thermodynamically possible. The article discusses the thermodynamics of phase transformations and free energy, as well as kinetics of phase transformations. It concludes with a description of solid-state phase transformations that occur when one or more parent phases, usually on cooling, produces a phase or phases.

This article reviews the general aspects of microstructure evolution during thermomechanical processing. The effect of thermomechanical processing on microstructure evolution is summarized to provide insight into the aspect of process design. The article provides information on hot working and key processes that control microstructure evolution: dynamic recovery, static recovery, recrystallization, and grain growth. Some of the key phenomenological descriptions of plastic flow and microstructure evolution are also summarized. The article concludes with a discussion on the modeling of microstructure evolution.

The cracking process occurs slowly over the service life from various crack growth mechanisms such as fatigue, stress-corrosion cracking, creep, and hydrogen-induced cracking. Each of these mechanisms has certain characteristic features that are used in failure analysis to determine the cause of cracking or crack growth. This article discusses the macroscopic and microscopic basis of understanding and modeling fracture resistance of metals. It describes the four major types of failure modes in engineering alloys, namely, dimpled rupture, ductile striation formation, cleavage or quasicleavage, and intergranular failure. Certain fundamental characteristics of fracture observed in precipitation-hardening alloys, ferrous alloys, titanium alloys are also discussed.

This article provides a brief description of the different types of micromechanisms of monotonic and cyclic fracture. General information on the material variables that have the most beneficial effect on resistance to failure is presented. The article discusses the various stages, growth rates, and striation spacings of fatigue crack. The mechanisms of fatigue striation formation are also discussed. The fatigue crack growth in duplex microstructures and cyclic crack growth in polymers are reviewed. The article also describes the mechanisms and models of fatigue crack closure.

Conventional high-strength aluminum alloys produced via powder metallurgy (P/M) technologies, namely, rapid solidification (RS) and mechanical alloying (mechanical attrition) have high strength at room temperature and elevated temperature. This article focuses on the metallurgy and weldability of dispersion-strengthened aluminum alloys based on the aluminum-iron system that are produced using various RS-P/M processing techniques. It describes weldability issues related to weld solidification behavior, the formation of hydrogen-induced porosity in the weld zone, and the high-temperature deformation behavior of these alloys, which affect the selection and application of fusion and solid-state welding processes. The article provides specific examples of material responses to welding conditions and highlights the microstructural development in the weld zone.