Search Results for cleavage fractures

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of miscellaneous metals and alloys and in identifying and interpreting the morphology of fracture surfaces. The metals and alloys covered include tungsten, iridium, magnesium-base, iron-base, molybdenum-base, and tantalum-base materials. The fractographs illustrate fatigue striations, slow-bending fracture, quasi-cleavage fracture, corrosion-fatigue fracture, fatigue crack, intergranular cleavage, microvoid coalescence, tension-overload fracture, crack propagation, impact fracture, and high-cycle fatigue failure.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of low-carbon steels and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the following: the intergranular fracture, bending impact fracture, brittle fracture, tensile-test fracture, transgranular fracture, cleavage fracture, delayed fracture, corrosion fatigue, inclusion morphology, fatigue crack propagation, and in-service fatigue fracture of various automotive components. These components include tie rod adjusting sleeves, automotive bolts, hydraulic jack shafts, crank handle collars, boiler tubes, drive shafts, bicycle pedal axles, lift-truck hydraulic-piston rods, and steel springs.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of AISI/SAE alloy steels (4xxx steels) and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the brittle fracture, ductile fracture, impact fracture, fatigue fracture surface, reversed torsional fatigue fracture, transgranular cleavage fracture, rotating bending fatigue, tension-overload fracture, torsion-overload fracture, slip band crack, crack growth and crack initiation, crack nucleation, microstructure, hydrogen embrittlement, sulfide stress-corrosion failure, stress-corrosion cracking, and hitch post shaft failure of these steels. The components considered in the article include tail-rotor drive-pinion shafts, pinion gears, outboard-motor crankshafts, bull gears, diesel engine bearing cap bolts, splined shafts, aircraft horizontal tail-actuator shafts, bucket elevators, aircraft propellers, helicopter bolts, air flasks, tie rod ball studs, and spiral gears.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of austenitic stainless steels and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the following: fatigue-crack fracture, rock candy fracture, cleavage fracture, brittle fracture, high-cycle fatigue fracture, fatigue striations, hydrogen-embrittlement failure, creep crack propagation, fatigue crack nucleation, intergranular creep fracture, torsional overload fracture, stress-corrosion cracking, and grain-boundary damage of these steels. The austenitic stainless steel components include spring wires, preheater-reactor slurry transfer lines and gas lines of coal-liquefaction pilot plants, oil feed tubes and suction couch rolls of paper machines, cortical screws and compression hip screws of orthopedic implants, and Jewett nails.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of pure irons and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the grain-boundary cavitation; slip lines; intergranular fracture; cleavage fracture; notch-impact fracture; oxide inclusions and blowholes; ductile rupture; impact fracture and tensile-test fracture surfaces; fatigue striations; and crack initiation and propagation of pure irons.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of titanium alloys and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the fracture surface, fatigue crack growth, intergranular fracture, crack propagation, ductile overload fracture, dimpled rupture, microvoid coalescence, and quasi-cleavage fracture of these alloys.

In this article, a basic summary of fracture mechanisms in carbon and alloy steels is presented, along with numerous examples of these fractures. These examples include ductile fracture, brittle cleavage fracture, intergranular fracture, fatigue fracture, and environmentally assisted failure mechanisms.