Alloy 5454 is an Al-Mg-Mn-Cr solid solution alloy with relatively high strength used for handling chemicals at elevated temperatures in the chemical and process industries. This datasheet provides information on key alloy metallurgy, processing effects on physical and mechanical properties, and fabrication characteristics of this 5xxx series alloy.

This article begins with the one-component, or unary, diagram for magnesium. The diagram shows what phases are present as a function of the temperature and pressure. When two metals are mixed in the liquid state to produce a solution, the resulting alloy is called a binary alloy. The article describes the various types of solid solutions such as interstitial solid solutions and substitutional solid solutions. Free energy is important because it determines whether or not a phase transformation is thermodynamically possible. The article discusses the thermodynamics of phase transformations and free energy, as well as kinetics of phase transformations. It concludes with a description of solid-state phase transformations that occur when one or more parent phases, usually on cooling, produces a phase or phases.

This article begins with a schematic illustration of a eutectic system in which the two components of the system have the same crystal structure. Eutectic systems form when alloying additions cause a lowering of the liquidus lines from both melting points of the pure elements. The article describes the aluminum-silicon eutectic system and the lead-tin eutectic system. It discusses eutectic morphologies in terms of lamellar and fibrous eutectics, regular and irregular eutectics, and the interpretation of eutectic microstructures. The article examines the solidification of a binary alloy of exactly eutectic composition. It concludes with a discussion on terminal solid solutions.

Precipitation reactions occur in many different alloy systems when one phase transforms into a mixed-phase system as a result of cooling from high temperatures. This article discusses the homogenous and heterogeneous nucleation and growth of coherent and semicoherent precipitates. It describes two precipitation modes, namely, general or continuous precipitation and cellular or discontinuous precipitation. The article also provides information on the precipitation sequences in aluminum alloys.

This article provides information on four different length scales at which surface morphology can be viewed: macro, meso, micro and nanoscale. Elementary thermodynamics demonstrates that a liquid cannot solidify unless some undercooling below the equilibrium (melting) temperature occurs. The article details five types of solidification undercooling, namely, kinetic, thermal, constitutional (solutal), curvature, and pressure undercooling. It explains the types of nucleation which occur in the melt during solidification. The effects of local instabilities at the solid/liquid interface during growth are illustrated. The article also describes the solidification structures of pure metals, solid solutions, eutectics, peritectics, and monotectics.

This article provides an overview of the metallurgical effects on corrosion of different series of aluminum alloys (1xxx, 2xxx, 3xxx, 4xxx, 5xxx, 6xxx, and 7xxx) that are classified into two categories. The first category includes the effects from insoluble, intermetallic constituent particles generally formed from trace impurity elements that play a predominant role in pitting corrosion. The second category comprises the effects from precipitation of secondary phases and effects from solute remaining in solid solution on corrosion of aluminum.