In general, metal-matrix composites (MMCs) are classified into three broad categories: continuous fiber-reinforced composites, discontinuous or short fiber-reinforced composites, and particle-reinforced composites. This article focuses on stir casting and melt infiltration as the two main methods of MMC solidification processing. It describes the MCC casting methods, such as sand and permanent mold casting, centrifugal casting, compocasting, and high-pressure die casting. The article discusses the MMC infiltration processes in terms of pressure infiltration casting and liquid metal infiltration. It reviews the powder metallurgy processing of aluminum MMCs and deformation processing of discontinuously reinforced aluminum composites. The article concludes with a discussion on the processing of fiber-reinforced aluminum.

This article describes the results of several case history studies of the failure of polymer-matrix composite components to provide not only some representative types of failures that can encounter, but also to provide some insight into the investigative process. These case histories deal mainly with structures that exhibit an initial material and/or manufacturing defect or failures that are most prevalent and most easily solved. The components include helicopter rotor blade, composite wing spar, and aircraft rudder.

This article discusses the dies, such as shear-face dies, conical-feed dies, and bridge dies, that are used in extrusion of particle-reinforced aluminum composites. It provides an overview of the effects of reinforcements on the properties of aluminum composites.

This article describes the types of closure mechanisms, including plasticity-induced, roughness-induced, oxide-induced, and fretting-debris-induced. It discusses test techniques used to establish a valid threshold value for aluminum alloy crack growth thresholds, steel crack growth thresholds, and titanium alloy crack growth thresholds. The near-threshold behavior of nickel-base superalloys is described. The article briefly reviews the threshold results for fiber-reinforced, whisker-reinforced, and particulate-re-inforced metal-matrix alloys. It explains the near-threshold fatigue crack propagation in welded joints and the fundamental considerations for modeling threshold behavior. The article concludes with a discussion on the effects of thresholds in the engineering design process.