This article addresses macroscale fracture appearances, microscale fracture-surface appearances or morphologies, fracture mechanisms, and those factors that influence fractures and fracture appearances. Some of the macroscopic and microscopic features identified by the failure analyst to evaluate the fracture surfaces of metals and plastics are described and compared.

Quantitative fractography (QF) is the examination and characterization of fracture surfaces of failed or broken-open components and specimens. This article provides examples of the application of QF to evaluate real-life fatigue failures and also a comprehensive guideline chart for detecting and measuring fatigue striations and progression markings, with examples.

This article presents the concept of fracture mechanisms in general terms in order to impart a practical understanding as well as enable readers to develop the ability to identify the basic fracture mechanisms correctly based on microscope observations. The key microscopic features of fracture surfaces are described and illustrated for the important types of fracture mechanisms. It provides a detailed discussion on environmentally assisted crack initiation and growth.

This article discusses several examples of fatigue load histories that intentionally create artificial fracture-surface markings during testing such that they are measurable by post-test quantitative fractography (QF). It reviews a number of methods for providing fatigue fracture-surface markers to aid QF of fatigue crack growth (FCG). These methods are based on load changes, including reordering the basic load histories and/or adding loads to them. The article also provides some guidelines for obtaining recognizable FCG markers for a variety of load histories and crack-growth regimes for coupons, components, and, particularly, full-scale fatigue tests.

In this article, a basic summary of fracture mechanisms in carbon and alloy steels is presented, along with numerous examples of these fractures. These examples include ductile fracture, brittle cleavage fracture, intergranular fracture, fatigue fracture, and environmentally assisted failure mechanisms.

This article provides an overview of fractography as it applies to metal weldments and presents examples of various fracture surface morphologies to demonstrate how fractographic analysis can be used to determine the cause of weld failures. It identifies weld fractography principles and details several weldment-specific geometric and metallurgical considerations. The role of the weld-cracking mechanisms on the resultant fracture surfaces is described, along with example micrographs and fractographs of weldments. Common discontinuities related to welding processes and their impact on the resulting fracture behavior and surfaces are covered, as well as the common fractographic features related to fatigue failures of welds.

This article presents the failure of polymer-matrix composites and the methodology for fractography. It provides a detailed discussion on the types of translaminar, interlaminar, and intralaminar failures. The article also presents a discussion on the types of fatigue failures, and the influence of composite architecture. It provides details of the fractography associated with defects and damage.

Structure-property relationships for metal additive manufacturing (AM) using solidification-based AM processes (e.g., powder-bed fusion and directed-energy deposition) are the focus of this article. Static strength and ductility properties in AM materials are impacted heavily by the microstructure but are also affected by porosity and surface roughness. Fatigue failure in AM materials is also influenced by porosity, surface roughness, microstructure, and residual stress due to applied manufacturing processing parameters. Post-processing treatments can further influence fatigue failure in AM materials.

This article reviews generalized test methodologies for fatigue characterization of polymers and examines fatigue fracture mechanisms in different engineering plastics. It provides detailed micromechanistic images of crack-tip processes for a variety of semicrystalline and amorphous engineering polymers. The article describes fracture mechanics solutions and approaches to the fatigue characterization of engineering polymers when dealing with macroscale fatigue crack growth. It includes mechanistic images for high-density polyethylene, ultrahigh-molecular-weight polyethylene, nylon 6, 6, polycarbonate, and polypropylene. The article describes the micromechanisms of toughening of plastics and uses a macroscale approach of applying fracture mechanics to the fatigue life prediction of engineering polymers, building on the mechanistic concepts. It also describes the factors affecting fatigue performance of polymers.

Failure of structural polymeric materials under cyclic application of stress or strain is a subject of industrial importance. The understanding of fatigue mechanisms (damage) and the development of constitutive equations for damage evolution, leading to crack initiation and propagation as a function of loading or displacement history, represent a fundamental problem for scientists and engineers. This article describes the approaches to predict fatigue life and discusses the difference between thermal and mechanical fatigue failure of polymers.

In addition to failures in shafts, this article discusses failures in connecting rods, which translate rotary motion to linear motion (and conversely), and in piston rods, which translate the action of fluid power to linear motion. It begins by discussing the origins of fracture. Next, the article describes the background information about the shaft used for examination. Then, it focuses on various failures in shafts, namely bending fatigue, torsional fatigue, axial fatigue, contact fatigue, wear, brittle fracture, and ductile fracture. Further, the article discusses the effects of distortion and corrosion on shafts. Finally, it discusses the types of stress raisers and the influence of changes in shaft diameter.

Mechanical springs are used in mechanical components to exert force, provide flexibility, and absorb or store energy. This article provides an overview of the operating conditions of mechanical springs. Common failure mechanisms and processes involved in the examination of spring failures are also discussed. In addition, the article discusses common causes of failures and presents examples of specific spring failures, describes fatigue failures that resulted from these types of material defects, and demonstrates how improper fabrication can result in premature fatigue failure. It also covers failures of shape memory alloy springs and failures caused by corrosion and operating conditions.

This article provides the framework for the investigation of bridge failures. It explains the types of bridge loading and presents the regulatory provisions for bridges. Some bridge failures in the U.S. that resulted in significant changes in bridge manufacturing, design, regulation, and/or maintenance are also discussed. In addition, the article provides information on traffic damage and fatigue cracking that result in bridge failures. The need for steels with better fracture toughness in bridge design is also discussed.

Thermomechanical fatigue (TMF) is the general term given to the material damage accumulation process that occurs with simultaneous changes in temperature and mechanical loading. TMF may couple cyclic inelastic deformation accumulation, temperature-assisted diffusion within the material, temperature-assisted grain-boundary evolution, and temperature-driven surface oxidation, among other things. This article discusses some of the major aspects and challenges of dealing with TMF life prediction. It describes the damage mechanisms of TMF and covers various experimental techniques to promote TMF damage mechanisms and elucidate mechanism coupling interactions. In addition, life modeling in TMF conditions and a practical application of TMF life prediction are presented.

Fatigue failure of engineering components and structures results from progressive fracture caused by cyclic or fluctuating loads. Fatigue is an important potential cause of mechanical failure, because most engineering components or structures are or can be subjected to cyclic loads during their lifetime. This article focuses on fractography of fatigue. It provides an abbreviated summary of fatigue processes and mechanisms: fatigue crack initiation, fatigue crack propagation, and final fracture,. Characteristic fatigue fracture features that can be discerned visually or under low magnification are then described. Typical microscopic features observed on structural metals are presented subsequently, followed by a brief discussion on fatigue in polymers and polymer-matrix composites.

Fatigue failures may occur in components subjected to fluctuating (time-dependent) loading as a result of progressive localized permanent damage described by the stages of crack initiation, cyclic crack propagation, and subsequent final fracture after a given number of load fluctuations. This article begins with an overview of fatigue properties and design life. This is followed by a description of the two approaches to fatigue, namely infinite-life criterion and finite-life criterion, along with information on damage tolerance criterion. The article then discusses the characteristics of fatigue fractures followed by a discussion on the effects of loading and stress distribution, and material condition on the microstructure of the material. In addition, general prevention and characteristics of corrosion fatigue, contact fatigue, and thermal fatigue are also presented.

This article provides a thorough review of the physical metallurgy of aluminum alloys and its role in determining the properties and from a design and manufacturing perspective. And its role in include the effects of composition, mechanical working, and/or heat treatment on structure and properties. This article focuses on the effects of alloying and the metallurgical factors on phase constituents, structure, and properties of aluminum alloys. Effects from different combinations of alloying elements are described in terms of relevant alloy phase diagrams. The article addresses the underlying alloying and structural aspects that affect the properties and possible processing routes of aluminum alloys. It provides information on the heat treatment effects on the physical properties of aluminum alloys and the microstructural effects on the fatigue and fracture of aluminum alloys. The important alloying elements and impurities are listed alphabetically as a concise review of major effects.

As cast iron parts are extensively applied, fracture events will eventually take place. Consequently, it becomes essential to carry out failure analyses to identify the cause of fracture and to provide corrective actions that allow safe operation. This article presents a description of the main fracture modes and their characteristic fractographic features. It discusses the four principal fracture modes: dimple rupture (or fracture), cleavage, fatigue, and intergranular fracture. The article provides information on special cases of environmentally assisted fracture. It concludes with a description of fractographic analyses for identifying the direction of propagation of a crack.

This article describes the formation of residual stresses and distortion and the techniques for measuring residual stresses. It provides a discussion on the magnitude and distribution analysis of residual stresses and distortion in weldments. The article considers the effects of residual stresses and distortion on the brittle fracture and fatigue fracture of welded structures. The thermal treatments of weldments are also discussed.