Failure of structural polymeric materials under cyclic application of stress or strain is a subject of industrial importance. The understanding of fatigue mechanisms (damage) and the development of constitutive equations for damage evolution, leading to crack initiation and propagation as a function of loading or displacement history, represent a fundamental problem for scientists and engineers. This article describes the approaches to predict fatigue life and discusses the difference between thermal and mechanical fatigue failure of polymers.

Fatigue failure of engineering components and structures results from progressive fracture caused by cyclic or fluctuating loads. Fatigue is an important potential cause of mechanical failure, because most engineering components or structures are or can be subjected to cyclic loads during their lifetime. This article focuses on fractography of fatigue. It provides an abbreviated summary of fatigue processes and mechanisms: fatigue crack initiation, fatigue crack propagation, and final fracture,. Characteristic fatigue fracture features that can be discerned visually or under low magnification are then described. Typical microscopic features observed on structural metals are presented subsequently, followed by a brief discussion on fatigue in polymers and polymer-matrix composites.

The purposes and methods of fatigue modeling and simulation in high-cycle fatigue (HCF) regime are to design either failsafe components or components with a finite life and to quantify remaining life of components with pre-existing cracks using fracture mechanics, with the intent of monitoring via an inspection scheme. This article begins with a discussion on the stages of the fatigue damage process. It describes hierarchical multistage fatigue modeling and several key points regarding the physics of crack nucleation and microstructurally small crack propagation in the HCF regime. The article provides a description of the microstructure-sensitive modeling to model fatigue of several classes of advanced engineering alloys. It describes the various modeling and design processes designed against fatigue crack initiation. The article concludes with a discussion on the challenges in microstructure-sensitive fatigue modeling.

This article provides a review of fatigue test methodologies and an overview of general fatigue behavior, fatigue crack initiation and fatigue crack propagation of advanced engineering plastics. It also describes the factors affecting fatigue performance of polymers and concludes with information on fractography, a useful tool in failure analysis.

This article presents an overview of fatigue crack nucleation from the point of view of the material microstructure and its evolution during cycling. It describes the sites of microcrack nucleation at the free surfaces. The article discusses the relation of dislocation structures and surface relief and reviews the mechanisms of crack nucleation. The damage of material due to crack nucleation, the extent (in terms of the number of cycles) of the nucleation stage, and the factors influencing crack nucleation are discussed.

This article describes the test techniques that are available for monitoring crack initiation and crack growth and for obtaining information on fatigue damage in test specimens. These techniques include optical methods, the compliance method, electric potential measurement, and gel electrode imaging methods. The article discusses the magnetic techniques that are primarily used as inspection techniques for detecting fatigue cracks in structural components. It details the principles and operation procedures of the liquid penetrant methods, positron annihilation techniques, acoustic emission techniques, ultrasonic methods, eddy current techniques, infrared techniques, exoelectron methods, and gamma radiography. The article explains the microscopy methods used to determine fatigue crack initiation and propagation. These include electron microscopy, scanning tunneling microscopy, atomic force microscopy, and scanning acoustic microscopy. The article also reviews the X-ray diffraction technique used for determining the compositional changes, strain changes, and residual stress evaluation during the fatigue process.

This article reviews the influence of local strains and corrosion fatigue on the initiation of fatigue cracks in duplex stainless steels. It provides useful information on fatigue crack growth, fatigue strength, and fracture toughness of duplex stainless steels. The article discusses the fatigue and fracture behavior of duplex stainless steels during stress-corrosion cracking. It details the elevated-temperature properties of duplex stainless steels, such as creep-fatigue behavior and thermal cycling properties.

Fatigue crack initiation is an important aspect of materials performance in design. This article summarizes some fundamental concepts and procedures for the fatigue life prediction of relatively homogeneous, wrought metals when a major portion of total life is exhausted in crack initiation. It presents an overview of the strain-based, as opposed to stress-based, criterion of material behavior and fatigue analysis. The article describes the cyclic stress-strain behavior of metals to illustrate the inadequacy of the monotonic or tensile stress-strain curve in accounting for material instabilities caused by cyclic deformations. It discusses the effect of mean stress on fatigue life and presents the analysis of cumulative fatigue damage. The article concludes with examples of application techniques for fatigue life prediction.

Fatigue damage in metals is caused by the simultaneous action of cyclic stress, tensile stress, and plastic strain. This article details the fundamental aspects of the stages of the fatigue failure process. These include cyclic plastic deformation prior to fatigue crack initiation, initiation of one or more microcracks, propagation or coalescence of microcracks to form one or more microcracks, and propagation of one or more macrocracks.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of P/M aluminum alloys (aluminum-lithium alloys) and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the fracture surface, and corrosion-fatigue crack initiation and propagation of these alloys.