This article presents fractographs that show evidence of overload in white cast irons. Images illustrate brittle fracture with cleavage facets and fracture at carbide boundaries, as well as cracks caused by shear stress and the tensile stress due to rebounding.

This article provides an overview of fractography and explains how it is used in failure analysis. It reviews the basic types of fracture processes, namely, ductile, brittle, fatigue, and creep, principally in terms of fracture appearances, such as microstructure. The article also describes the general features of fatigue fractures in terms of crack initiation and fatigue crack propagation.

Overload failures refer to the ductile or brittle fracture of a material when stresses exceed the load-bearing capacity of a material. This article reviews some mechanistic aspects of ductile and brittle crack propagation, including a discussion on mixed-mode cracking, which may also occur when an overload failure is caused by a combination of ductile and brittle cracking mechanisms. It describes the general aspects of fracture modes and mechanisms. The article discusses some of the material, mechanical, and environmental factors that may be involved in determining the root cause of an overload failure. It also presents examples of thermally and environmentally induced embrittlement effects that can alter the overload fracture behavior of metals.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of miscellaneous metals and alloys and in identifying and interpreting the morphology of fracture surfaces. The metals and alloys covered include tungsten, iridium, magnesium-base, iron-base, molybdenum-base, and tantalum-base materials. The fractographs illustrate fatigue striations, slow-bending fracture, quasi-cleavage fracture, corrosion-fatigue fracture, fatigue crack, intergranular cleavage, microvoid coalescence, tension-overload fracture, crack propagation, impact fracture, and high-cycle fatigue failure.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of wrought aluminum alloys and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the corrosion-fatigue fracture, fatigue striations, tension-overload fracture surface, ductile fracture, cone-shaped fracture surface, intergranular crack propagation, transgranular crack propagation, stress-corrosion cracking, hydrogen damage, and grain-boundary separation of these alloys. Fractographs are also provided for a forged aircraft main-landing gear wheel and actuator beam, an aircraft wing spar, a fractured aircraft propeller blade, shot peened fillet, an aircraft lower-bulkhead cap, and clevis-attachment lugs.

This article is an atlas of fractographs that helps in understanding the causes and mechanisms of fracture of AISI/SAE alloy steels (4xxx steels) and in identifying and interpreting the morphology of fracture surfaces. The fractographs illustrate the brittle fracture, ductile fracture, impact fracture, fatigue fracture surface, reversed torsional fatigue fracture, transgranular cleavage fracture, rotating bending fatigue, tension-overload fracture, torsion-overload fracture, slip band crack, crack growth and crack initiation, crack nucleation, microstructure, hydrogen embrittlement, sulfide stress-corrosion failure, stress-corrosion cracking, and hitch post shaft failure of these steels. The components considered in the article include tail-rotor drive-pinion shafts, pinion gears, outboard-motor crankshafts, bull gears, diesel engine bearing cap bolts, splined shafts, aircraft horizontal tail-actuator shafts, bucket elevators, aircraft propellers, helicopter bolts, air flasks, tie rod ball studs, and spiral gears.