Seals are mechanical components that prevent the leakage, diffusion, transfer, or mixing of different liquid, gas, solid, and multiphasic substances. This article begins by discussing the classifications of seals: static and dynamic. Static seals involve both self-energizing elastomeric materials such as O-rings, which merely react to a sealed fluid pressure, and passive materials that require clamping forces to achieve sealing, such as gaskets. The types of dynamic seals include rotary seals and reciprocating seals. The article describes the factors affecting seal wear and failure. It provides a list of some common seal wear modes and failures, namely abrasion, cavitation damage, chemical attack, compression set, corrosion, damage during abrupt decompression, dieseling damage, extrusion damage, installation damage, spiral or rolling damage, and vaporization damage. The article concludes with specific recommendations for reducting of seal friction and wear.

This article focuses on the modeling and simulation of cavitation phenomena. It summarizes the experimental observations of cavitation and reviews the modeling of cavity nucleation and growth. The article discusses the modeling of the cavity growth based on mesoscale and microscale under uniaxial versus multiaxial tensile-stress conditions. Mesoscale models incorporate the influence of local microstructure and texture on cavitation. The article outlines the descriptions of cavity coalescence and shrinkage. It also describes the simulation of the tension test to predict tensile ductility and to construct failure-mechanism maps.

Advances in vehicle design and technology require engine coolant technology to minimize the degradation of nonmetals and prevent the corrosion of the metals in the cooling system. This article provides a detailed discussion on the functions, operation, materials, and major components of the cooling system. It discusses various forms of corrosion that occur in cooling systems, including uniform corrosion, galvanic corrosion, crevice corrosion, pitting corrosion, intergranular corrosion, erosion corrosion, and cavitation corrosion. The article presents information on engine coolant base components and inhibitors used for corrosion prevention. It reviews the coolant performance tests recommended by ASTM, SAE, and vehicle manufacturers. The article concludes with a description on the difference between light-duty automotive and heavy-duty diesel engine coolants.

This article discusses two types of hot-tension tests, namely, the Gleeble test and conventional isothermal hot-tension test, as well as their equipment. It summarizes the data for hot ductility, strength, and hot-tension for commercial alloys. The article presents isothermal hot-tension test data, which helps to gain information on a number of material parameters and material coefficients. It details the effect of test conditions on flow behavior. The article briefly describes the detailed interpretation of data from the isothermal hot-tension test using numerical model. It also explains the cavitation mechanism and failure modes that occur during hot-tension testing.

Erosion, cavitation, and impingement are mechanically assisted forms of material degradation that often contribute to corrosive wear. This article identifies and describes several tests that are useful for ranking the service potential of candidate materials under such conditions. The tests, designed by ASTM as G32, G73, G75, and G76, define specimen preparation, test conditions, procedures, and data interpretation. The article examines the relative influence of various test parameters on the incubation and intensity of cavitation, including temperature, pressure, flow velocity, and vibration dynamics. It concludes with a discussion on data correlations and the relationship between laboratory results and service expectations.

This article outlines the processes by which materials are selected to prevent or control localized corrosion, galvanic corrosion, and intergranular corrosion. It reviews the operating conditions and the design of candidate materials for material selection. The article discusses various corrosion-resistant materials, including ferrous and nonferrous metals and alloys, thermoplastics, reinforced thermosetting plastics, nonmetallic linings, glass, carbon and graphite, and catalyzed resin coatings. It examines an unusual form of intergranular corrosion known as exfoliation, which occurs in aluminum-copper alloys. The article also describes three types of erosion-corrosion: liquid erosion-corrosion, cavitation, and fretting. It concludes with information on the various factors to be considered for material selection, including minimum cost or economic design, minimum corrosion, minimum investment, and minimum maintenance.

Mechanically assisted degradation of metals is defined as any type of degradation that involves a corrosion mechanism and a wear or fatigue mechanism. This article provides a discussion on the mechanisms of five forms of degradation: erosion, fretting corrosion, fretting fatigue, cavitation and water drop impingement, and corrosion fatigue. It describes the factors affecting the severity of fretting corrosion. The article also illustrates the relationship between corrosion fatigue and stress-corrosion cracking.

This article discusses corrosion resistance of titanium and titanium alloys to different types of corrosion, including galvanic corrosion, crevice corrosion, stress-corrosion cracking (SCC), erosion-corrosion, cavitation, hot salt corrosion, accelerated crack propagation, and solid and liquid metal embrittlement. A short section discusses the addition of alloys that can improve the corrosion resistance of titanium.