This article presents fractographs that show evidence of overload and fatigue in gray cast irons. The overload failure section illustrates a fractured motor housing, valve body, and bracket with microvoid coalescence (dimpled rupture) in the metal matrix between graphite flakes. The fractographs of fatigue failures illustrate a gearbox housing with fatigue striations and pearlitic microstructure.

This article presents fractographs of overload fractures in a ductile cast iron piston, tensile test bar, differential case, brake caliper, compressor crankshaft, and pivot arm. SEM images show such features as dimpled rupture at the thin metallic matrix ligatures between the graphite nodules, bull's-eye ferrite and pearlite microstructure, loose graphite nodules and dimpled rupture morphology transitioning to cleavage, cleavage morphology with river lines, and ratchet marks and beach marks.

This article presents fractographs of pure irons that show evidence of overload, fatigue, and embrittlement. Woody fracture, microvoid coalescence, cleavage, and stress rupture are seen in the overload failure images. A large inclusion is seen in the fatigue fractograph. Embrittlement images show an impact fracture with intergranular rupture and transcrystalline cleavage.

With regard to documentation and photography of a catastrophic event, the field investigator's duties are fundamentally different from those of the laboratory-based analyst, even though both share the same goals. This article presents a case study on documentation considerations during the field investigation. It provides a detailed discussion on the general procedure to downselect from a multicomponent assemblage to a set of potential primary failed components. The article describes visual examination in macrofractography.

Fracture surfaces can provide an important and indispensable record of many factors in simple or complex failures. Visual examination of fracture surfaces can reveal the type and direction of loading, with fracture-surface features often providing definitive evidence of torsion, tension, bending, and compressive loads. This article discusses tools and techniques of visual examination and characteristic features of fracture features. A brief review of ductile and brittle fracture-surface features is provided. The article also describes macroscopic features that can be used to identify fracture-initiation sites, locations of final overload, and the directions of crack propagation. In addition, the use of these features to characterize loading at the time of failure is also described.

The introduction of focused ion beam (FIB) microscopy in the 1990s added the capability of studying fracture surfaces in the third dimension and making site-specific and stress-free transmission electron microscope (TEM) specimens in situ. This article reviews the methods for preparing replicas and the site-specific FIB thin-foil preparation technique. It provides an overview of FIB-TEM specimen preparation.

This article provides a discussion on the following photographic equipment: point-and-shoot cameras, digital single-reflex cameras, stand-mounted digital zoom cameras, and digital microscope cameras. It presents two principal types of optical microscopes that are appropriate for visual examination of fractured parts: the stereomicroscope and the single-light-path digital microscope. The common features present on fracture surfaces are each considered separately, both in their significance and as photographic challenges. The article also presents a short note on low-magnification scanning electron microscopy and postcapture image processing.

This article discusses the importance of the care and handling of fracture specimens and what to look for during the preliminary field or laboratory observation and collection, the preservation of specimens, and the cleaning and preparation of fracture specimens for additional analyses. The preservation of nonmetallic specimens, medical devices, oversized components, light alloys, nondestructively tested components, and materials that are part of legal proceedings is addressed.

This article presents a basic overview of technology-driven advances in the imaging of primarily metallic fracture surfaces. It describes various types of microscopes, including scanning electron, dual-beam, ion source, and transmission electron microscopes, and their capabilities. It also covers other useful hardware, such as computer-aided tomography (CAT) and micro-computer-aided tomography (micro-CAT) instruments. The article introduces some of the fracture image postprocessing methods and software, including image registration or alignment, focus stacking, Z-stacking, focal plane merging, and image stitching.

This article presumes the reader has a basic understanding of the operation and principles of scanning electron microscopy (SEM). The emphasis of this article is specifically on the application of SEM to the study of metallic and nonmetallic fracture surfaces, where the typical objectives of SEM examination of a fracture surface may include the following: identification of characteristic fracture features to aid in identifying fracture mechanism(s); characterization of material anomalies that may have influenced the fracture; qualitative or semiquantitative chemical analysis of component material(s); and qualitative or semiquantitative analysis of deposits or corrosion products on or near fracture surfaces.

The development of quantitative fractography (QF) parameters basically requires topological data of a fracture surface that can be derived from the stereological analysis of multiple projected scanning electron microscope (SEM) images; the profilometry-based techniques that measure the fracture surface profile along x-y sections of a fracture surface from metallographic sections or nondestructive techniques; and the three-dimensional reconstruction of the fracture surface topology using imaging methods such as stereo SEM imaging and confocal scanning laser microscopy. These three general methods of assessing fracture surface topology are reviewed in this article.

This article discusses several examples of fatigue load histories that intentionally create artificial fracture-surface markings during testing such that they are measurable by post-test quantitative fractography (QF). It reviews a number of methods for providing fatigue fracture-surface markers to aid QF of fatigue crack growth (FCG). These methods are based on load changes, including reordering the basic load histories and/or adding loads to them. The article also provides some guidelines for obtaining recognizable FCG markers for a variety of load histories and crack-growth regimes for coupons, components, and, particularly, full-scale fatigue tests.

This article provides an overview of polymer fractography, with examples of various fracture surfaces created under diverse loading conditions. The focus is on the interpretation of polymer fracture-surface features in light of the unique viscoelastic nature of polymers. The article presents fractographic examples of three time-dependent cracking mechanisms: fatigue fracture, creep rupture, and environmental stress cracking. It details characteristic fractographic features that can be observed in optical microscopy (OM) and scanning electron microscopy (SEM).

This article discusses fractures and cracks due to ancient artifact weaknesses. It provides several case studies to aid the appreciation of fractography as a diagnostic technique and to understand the importance of cracking. These case histories concern ancient gold and silver alloys, bronzes, and wrought irons. The article considers the applicabilities of fractography, metallography, and chemical analyses in answering archaeological and archaeometallurgical questions. The article also discusses the restoration and conservation of corroded and embrittled artifacts, including the use of coatings.

Many metal failures involve fracture, and fractography is an essential activity in many, if not most, failure analysis (FA) investigations. This article introduces and illustrates the role of fractography in an FA investigation. Basic guidelines are briefly presented for investigating a failure and how fractography helps the FA investigator determine evidence. Examples are given throughout this article on how the examination of fracture surfaces discerns various sources of crack initiation and mechanisms of crack growth. The procedures for analyzing fractures also include several steps and techniques that involve photographic documentation, proper specimen handling, and visual or microscopic examination. The article also briefly describes the use of metallography in fracture analysis along with case studies as illustrative examples of various fracture mechanisms and modes.

This article discusses an experimental setup and a measuring setup for capturing acoustic emission during quenching. It presents the procedure for sound-emission measurement and an analysis of the acoustic spectrum obtained during quenching.

This article explains cooling mechanisms involving saltwater solutions used as quenchants. The analyses of cooling power include studies of cooling curves, heat-transfer coefficients, and cooling rates. The influence of other bath parameters, such as temperature and agitation, is also discussed. The article discusses solute additions and several factors impacting quenching.

The role of a mixer/agitator in quenching applications is to control the mixing environment in order to meet the process criteria. This article provides the basic fundamentals of the sizing of agitators, tank geometry importance, and other considerations for the application of agitators in quench tanks. It also discusses the differing methods for the sizing and selection of agitators for quench tank applications.

Computational fluid dynamics (CFD) provides an efficient, alternate, virtual approach for simulating and analyzing quenching processes with an impact on component design, manufacturing process, and quality. This article provides domain insights for quenching researchers and CFD practitioners for the modeling of the industrial quenching process and for supporting the diverse multifunctional needs in an industry, ranging from primary metallurgical companies (steel, aluminum, and other alloys), original equipment manufacturers, engineering companies, captive and commercial heat treating facilities, quench system manufacturers, and quench fluid suppliers. It describes the governing differential equations for the fluid flow and heat-transfer phenomena during quenching. The article also discusses different modeling categories to determine a CFD methodology for quenching.