Brittle Fracture of a Clamp Because of Burning During Forging
A ring clamp (8740 (AMS 6322), steel forged and cadmium plated) used for attaching ducts to an aircraft engine became loose after three hours of service. When the clamp was removed from the engine, the hinge tabs on one clamp half were found to be broken. Analysis (visual inspection and microscopic and metallographic examination) supported the conclusion that both hinge tabs on the clamp half fractured in a brittle manner as the result of gross overheating, or burning, during forging. The mechanical properties of the metal, especially toughness and ductility, were greatly reduced by burning. Evidence that burning was...
Brittle Fracture of a Clamp Because of Burning During Forging, ASM Failure Analysis Case Histories: Processing Errors and Defects, ASM International, 2019, https://doi.org/10.31399/asm.fach.process.c0047176