The cause of the fatigue failure in the retaining ring of the compressor region of an aero-engine turbine was found to be the presence of a high concentration of nonmetallic inclusions. The results of chemical analysis were used to estimate the phases present. The most frequently observed inclusions were spinel solid solutions of the type MO middot; N2O3, where M = Fe, Mn, or Mg and N = Cr or Al. The detrimental inclusions were corundum, calcium aluminates, cristobalite, and silicates. The most detrimental phases were traced on the surfaces of the specimens fractured using impact loading; the comparison...