ASM Failure Analysis Case Histories: Air and Spacecraft
Landing Gear and Undercarriage Components
-
Published:2019
Abstract
One main undercarriage axle made of high strength alloy steel was subjected to simulated fatigue test for 6000 h of service. After only 300 h it broke in two along the sharp radius. The fracture revealed a coarse, irregular, and brittle surface before final fracture by thick angular shear lip zone. The presence of micropores in the cleavage facets as well as at the grain boundaries and hairline type crack indications under SEM examination were all suggestive of hydrogen embrittlement. On the basis of investigation results and observations, it was concluded that the transverse breakage of the axle had...
Sign in
ASM members
Member Sign InLanding Gear and Undercarriage Components, ASM Failure Analysis Case Histories: Air and Spacecraft, ASM International, 2019
Download citation file:
ASM Technical Books
ASM Technical Books offer a wealth of materials science and engineering knowledge from experts in the field. Discover hundreds of practical guides and reference resources on a wide variety of subjects.