Use of Fractography for Failure Analysis
-
Published:1998
Abstract
This article describes various evaluation techniques of fractography such as visual inspection, macroscopic and microscopic examinations that are used to resolve different aspects of failure. It gives a brief description and pictorial representation of various defects leading to fracture of metals, including laps, seams, cold shuts, cracks, inclusions, porosity, fatigue, and stress corrosion cracking.
You do not currently have access to this chapter.
Citation
Use of Fractography for Failure Analysis, Metals Handbook Desk Edition, 2nd ed., Edited By Joseph R. Davis, ASM International, 1998, p 1248–1253, https://doi.org/10.31399/asm.hb.mhde2.a0003227
Download citation file:
October 16-19 | Detroit, Michigan
Keep up to date with the latest materials and processing technologies. Register today for IMAT 2023 & Heat Treat 2023!
Related Book Content
The Failure Analysis Process
Fatigue and Fracture Understanding the Basics
Failure of Aircraft Engine Compressor Rotors
Failure Analysis of Engineering Structures Methodology and Case Histories
Failure of a Second-Stage Compressor Blade in an Aircraft Engine
Failure Analysis of Engineering Structures Methodology and Case Histories
Fatigue Fracture Appearances
Failure Analysis and Prevention
Failure Analysis of Stress-Corrosion Cracking
Stress-Corrosion Cracking: Materials Performance and Evaluation (Second Edition)
Examination Methods
Failure Analysis of Engineering Structures Methodology and Case Histories
Failure of a Main Wheel Bearing Housing Flange in an Aircraft
Failure Analysis of Engineering Structures Methodology and Case Histories
Failure of a Stabilizer Link Rod in an Aircraft
Failure Analysis of Engineering Structures Methodology and Case Histories
Failure of a Wing Control Cable in an Aircraft
Failure Analysis of Engineering Structures Methodology and Case Histories
Failure of a Tail Rotor Blade in a Helicopter
Failure Analysis of Engineering Structures Methodology and Case Histories