Fatigue Crack Growth under Variable-Amplitude Loading
By
J. Schijve
J. Schijve
Delft University of Technology
Search for other works by this author on:
-
Published:1996
Abstract
This article summarizes fatigue phenomena in metallic materials. It discusses fatigue under variable-amplitude (VA) loading, with emphasis on crack growth. The article presents the prediction models of crack initiation and crack growth under VA loading. It concludes with a discussion on the conditions associated with engineering applications of VA loading.
You do not currently have access to this chapter.
Citation
J. Schijve, Fatigue Crack Growth under Variable-Amplitude Loading, Fatigue and Fracture, Vol 19, ASM Handbook, By ASM Handbook Committee, ASM International, 1996, p 110–133, https://doi.org/10.31399/asm.hb.v19.a0002356
Download citation file:
New Handbook: Volume 24A
Volume 24A provides a comprehensive review of additive manufacturing design fundamentals and applications.
Related Book Content
Fracture Toughness and Fracture Mechanics
Mechanical Testing and Evaluation
Mechanism of Fatigue
Fatigue and Durability of Structural Materials
Life Assessment of Steam-Turbine Components
Damage Mechanisms and Life Assessment of High-Temperature Components
Predictive Modeling of Structure Service Life
Corrosion: Fundamentals, Testing, and Protection
Fatigue and Fracture Mechanics
Mechanical Testing and Evaluation
Thermal and Thermomechanical Fatigue of Structural Alloys
Fatigue and Fracture
Abrasive Wear Failures
Failure Analysis and Prevention (2021 Edition)
Fracture and Structure
Fatigue and Fracture
Fatigue Spectrum Editing
Mechanics and Mechanisms of Fracture An Introduction
Mechanisms of Stress-Corrosion Cracking
Stress-Corrosion Cracking: Materials Performance and Evaluation (Second Edition)