Fracture Appearance and Mechanisms of Deformation and Fracture
By
W.T. Becker
;
W.T. Becker
University of Tennessee, Emeritus
Search for other works by this author on:
-
Published:2002
Abstract
This article provides an overview of fractography and explains how it is used in failure analysis. It reviews the basic types of fracture processes, namely, ductile, brittle, fatigue, and creep, principally in terms of fracture appearances, such as microstructure. The article also describes the general features of fatigue fractures in terms of crack initiation and fatigue crack propagation.
Topics
Corrosion,
Material failure analysis,
Wear,
Formability testing,
Life assessment testing,
Root cause analysis,
Microstructure,
Deformation and fracture,
Brittle fracture,
Intergranular fracture,
Transgranular fracture,
Crack initiation,
Fatigue crack propagation,
Creep fracture,
Ductile fracture,
Fatigue fracture,
Fractography,
Failure mechanisms and analysis
You do not currently have access to this chapter.
Citation
W.T. Becker, S. Lampman, Fracture Appearance and Mechanisms of Deformation and Fracture, Failure Analysis and Prevention, Vol 11, Edited By William T. Becker, Roch J. Shipley, ASM International, 2002, p 559–586, https://doi.org/10.31399/asm.hb.v11.a0003537
Download citation file:
Related Book Content
Fracture Appearance and Mechanisms of Deformation and Fracture
Failure Analysis and Prevention (2021 Edition)
Fracture of Plastics
Characterization and Failure Analysis of Plastics
Metallography: An Introduction
Metallography and Microstructures
Fracture and Fractography
Characterization and Failure Analysis of Plastics
Fatigue Failure of Six Cap Screws From a Hydraulic Coupling
Handbook of Case Histories in Failure Analysis
Failure Analysis of Wire Rope
ASM Failure Analysis Case Histories: Material Handling Equipment
Fatigue Testing and Behavior of Plastics
Mechanical Testing and Evaluation
Titanium Alloys: Atlas of Fractographs
Fractography
Low-Carbon Steels: Atlas of Fractographs
Fractography