Malleable Cast Irons
-
Published:2025
Page range:
1
Abstract
This article presents fractographs that show evidence of overload in a ferritic malleable cast iron. The images illustrate crack initiation and propagation, as well as regions of dimpled rupture.
You do not currently have access to this chapter.
Citation
Malleable Cast Irons, Atlas of Fractographs, Vol 12A, ASM Handbook, Edited By Craig J. Schroeder, Ronald J. Parrington, Joseph O. Maciejewski, James F. Lane, ASM International, 2025, p 1, https://doi.org/10.31399/asm.hb.v12a.a0007066
Download citation file:
Join ASM International
Being a member of the world’s largest association of materials professionals provides the benefits and resources you need to accomplish your personal and professional goals.
Related Book Content
Gray Cast Irons
Atlas of Fractographs
Mechanisms of Stress-Corrosion Cracking
Stress-Corrosion Cracking: Materials Performance and Evaluation (Second Edition)
Stress-Corrosion Cracking
Corrosion in the Petrochemical Industry (Second Edition)
Stress-Corrosion Cracking
Corrosion: Fundamentals, Testing, and Protection
Fatigue Testing and Behavior
Characterization and Failure Analysis of Plastics
Fatigue Failure
Characterization and Failure Analysis of Plastics
Malleable Irons/White Irons: Atlas of Fractographs
Fractography
Fatigue Strength of Metals
Mechanics and Mechanisms of Fracture An Introduction
Failure of Aircraft Wing Leading Edge Panel
ASM Failure Analysis Case Histories: Air and Spacecraft
Fracture and Structure
Fatigue and Fracture