Failure of a Reactor Tube
A low-carbon steel (St35.8) tube in a phthalic anhydride reactor system failed. Visual and stereomicroscopic examination of fracture surfaces revealed heavy oxide/deposits on the outer surface of the tube, tube wall thinning in the area of the fracture, and discolorations and oxides/deposits on the inner surface. Cross sections from the fracture surface were metallographically examined, and the deposits were analyzed. It was determined that the tube had thinned from the inner surface because of a localized overheating condition (probably resulting from a runaway chemical reaction within the tube) and then fractured, which allowed molten salt to flow into the tube.
J. Ciulik, Failure of a Reactor Tube, Handbook of Case Histories in Failure Analysis, Vol 2, Edited By Khlefa A. Esaklul, ASM International, 1993, p 187–191, https://doi.org/10.31399/asm.fach.v02.c9001333
Download citation file:
New Handbook: Volume 11B
Now available in the Digital Library! Volume 11B serves as a reference and guide to help engineers determine the causes of failure in plastic components and make corrective adjustments through design and manufacturing modifications.