Corrosion: Fundamentals, Testing, and Protection
This article discusses the basic approach for predicting the corrosion-fatigue life of structural components. It describes two types of tests that are normally used in combination: cycles-to-failure tests, which focus on crack initiation, and crack propagation tests, which focus on crack growth rates under cyclic load. The article examines corrosion-fatigue cracking along with the effects of cracking due to stress corrosion and hydrogen embrittlement, which often occur together. It explains how test parameters such as loading and environmental conditions impact crack growth mechanisms and data interpretation.
Bopinder Phull, Evaluating Corrosion Fatigue, Corrosion: Fundamentals, Testing, and Protection, Vol 13A, ASM Handbook, Edited By Stephen D. Cramer, Bernard S. Covino, Jr., ASM International, 2003, p 625–638, https://doi.org/10.31399/asm.hb.v13a.a0003668
Download citation file:
FALL / WINTER 2020 CATALOG
View the new, upcoming, and best-selling resources in ASM Handbooks, technical books, and databases in the Fall / Winter 2020 Catalog.