Abstract

The tail rotor blade of a helicopter developed a visible crack during service. The cracked region was removed from the blade and the fracture surface was examined in a SEM, revealing shallow pitting on the inside surface of the skin and a corresponding reduction in thickness. Based on these findings, investigators concluded that the failure was due to a fatigue crack initiated from a corrosion pit, which may have been caused by chemicals released by the burning of bonding resin.

You do not currently have access to this chapter.
Don't already have an account? Register

Cracking in a Tail Rotor Blade in a Helicopter, Failure Analysis of Engineering Structures: Methodology and Case Histories, By V. Ramachandran, A.C. Raghuram, R.V. Krishnan, S.K. Bhaumik, ASM International, 2005, p 156–157, https://doi.org/10.31399/asm.tb.faesmch.t51270156