1-20 of 122 Search Results for

welding parameter

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.bldgs.c9001611
EISBN: 978-1-62708-219-8
... Abstract Cold cracking of structural steel weldments is a well-documented failure mechanism, and extensive work has been done to recognize welding and materials selection parameters associated with it. These efforts, however, have not fully eliminated the occurrence of such failures...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001909
EISBN: 978-1-62708-235-8
... parameters resulted in acceptable welds. Bombs (weapons) Bomb fins Welded joints Weld defects Low-carbon steel Joining-related failures Reference 1. Anon .: in Welding Handbook , 8th ed. , vol. 1 , Welding Technology, Connor L.P. , ed., American Welding Society , Miami...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001304
EISBN: 978-1-62708-215-0
... of welding parameters, and failure was attributed to weld defects. References References 1. “Specification for Corrosion Resisting Chromium and Chromium-Nickel Bare and Composite Metal Cored and Stranded Welding Electrodes and Rods,” AWS A5.9–81, American Welding Society 2. Kou S...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.auto.c9001514
EISBN: 978-1-62708-218-1
... for the severity of the injuries sustained by the driver. The faulty welds in the unit body were apparently a consequence of improper settings of parameters on a multihead electrical resistance spot welding machine. Lack of appreciation of the hazard associated with failure of this weldment may have contributed...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001047
EISBN: 978-1-62708-214-3
... sheet joint allowed the Nox to condense and subsequently reboil. This, coupled with repeated repair welding in the area, reduced resistance to acid attack. Intergranular corrosion continued until failure. Recommendations included changing operating parameter inlet to prevent HNO3 condensation outside...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c9001735
EISBN: 978-1-62708-220-4
... examined metallographically on transverse sections and on longitudinal sections through the butt welds joining the separate cast segments of the tube. Creep damage was mainly concentrated within the inner one third of the wall thickness. The use of damage assessment parameters in evaluating the reformer...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001837
EISBN: 978-1-62708-241-9
... in combination with thermal stresses and constraint conditions, resulted in intergranular brittle fracture. welded nozzle assembly brittle fracture localized heating chromium alloy steel transgranular cleavage dimple rupture dye penetrant testing welding parameters 0.1%C-1.25%Cr-0.8%Mo-0.2%V steel...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001358
EISBN: 978-1-62708-215-0
... and postweld stress-relief temperatures. The same welding parameters (heat input, electrode size, etc.) were used for each experimental weld. Table 1 shows average microhardness results for the weld metal, HAZ, and base metal of the experimental welds and the actual welds. The results indicate...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001840
EISBN: 978-1-62708-241-9
... chamber ( Fig. 3b , c ), and explosive cladding was carried out safely. Regarding the explosive welding parameter window plotted for studying materials and after running several dry tests, the range of welding parameters (load ratio and stand off distance as main parameters) at which the visually sound...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001766
EISBN: 978-1-62708-241-9
... roadway. Post-failure analysis revealed that the fracture was precipitated by a preexisting weld-related crack. Closed form and numerical stress analyses were also conducted, with the results indicating that the anchor was installed properly within the parameters intended by the manufacturer...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001315
EISBN: 978-1-62708-215-0
... reactors Fast reactors Nuclear reactor components Welded joints Welding parameters AM350 UNS S35000 Joining-related failures ...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c0047681
EISBN: 978-1-62708-229-7
... in the electrode force, or both. Compressors Gas turbine engines Welding parameters Ti-6Al-4V UNS R56406 Joining-related failures Fatigue fracture ...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c0047673
EISBN: 978-1-62708-217-4
... weld-tool positioning. The problem could be solved by better forming procedures to provide an accurate fit-up that would not interfere with electrode alignment. Aircraft components Fuel tanks Welding parameters 2024-T62 UNS A92024 Joining-related failures A series of resistance spot...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.usage.c0047586
EISBN: 978-1-62708-236-5
... electrodes Welding parameters 321 UNS S32100 Joining-related failures ...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c0047566
EISBN: 978-1-62708-235-8
... equipment Filler metal Welding parameters 502 UNS S50200 Joining-related failures Handles welded to the top cover plate of a chemical-plant downcomer broke at the welds when the handles were used to lift the cover. The handles were fabricated of 19-mm ( 3 4 -in.) diam low-carbon steel rod...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.rail.c0048087
EISBN: 978-1-62708-231-0
... of the assembly. Cracks in weld regions of other portions of the assembly were found by magnetic-particle inspection. Heat affected zone Martensite Shielded metal arc welding Vibrations Welded joints Welding parameters 1020 1050 UNS G10200 UNS G10500 Fatigue fracture ...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001089
EISBN: 978-1-62708-214-3
.... It was recommended that crosshead castings be properly inspected before machining. Revision of foundry practice to reduce or eliminate porosity was also recommended. Compressors Porosity Repair welding Welded joints Welding parameters ASTM A148 grade 105-85 UNS D50800 Joining-related failures Casting...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001129
EISBN: 978-1-62708-214-3
..., would have prevented the failure. Heat-affected zone Low-cycle fatigue Welded joints Welding parameters Weldments Fe-0.25C-1.24Mn-0.62Cr-0.24Mo Fatigue fracture Joining-related failures Background Visual Examination of General Physical Features Testing Procedure and Results...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001061
EISBN: 978-1-62708-214-3
... Pipe, corrosion Pulping Welded joints, corrosion Welding parameters Carbon steel Joining-related failures Intergranular fracture Stress-corrosion cracking Intergranular corrosion Background Visual Examination of General Physical Features Testing Procedure and Results Discussion...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001055
EISBN: 978-1-62708-214-3
... lines. Certified test results from the steel mill, procedure qualification tests of the welding, and design changes to reduce water hammer were also recommended. Impact toughness Notch sensitivity Pipe joints Pipe Water pipelines Welding parameters ASTM A283 grade D UNS K02702 Joining...