1-20 of 22 Search Results for

stainless steel (duplex wrought stainless steel)

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001819
EISBN: 978-1-62708-241-9
... analysis fatigue strength stainless steel (duplex wrought stainless steel) 316 (austenitic wrought stainless steel) UNS S31600 Introduction Methodology Results and Discussion Conclusion References References 1. “ Petroleum and natural gas industries—Materials for use in H2S...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.pulp.c0091622
EISBN: 978-1-62708-230-3
... buildup. If redesign was impossible, an alloy more resistant to Cl-SCC, such as a duplex stainless steel or a high-molybdenum (4 to 6%) austenitic stainless steel, should be used. Chlorides Digesters Paper machines CF-8M UNS J92900 Stress-corrosion cracking A CF-8M (cast type 316) neck...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001773
EISBN: 978-1-62708-241-9
.... , Deverell H.E. , Redmond J.D. : Ferritic and duplex stainless steels . In: Process Industries Corrosion . National Association of Corrosion Engineers , Houston ( 1986 ) 3. Sedriks A.J. : Stress corrosion cracking of stainless steels . In: Stress corrosion cracking . ASM...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003553
EISBN: 978-1-62708-180-1
... steel chemical analysis copper alloys crack initiation crack propagation duplex stainless steel ferritic stainless steel fracture surface characteristics low alloy steel macroscopic examination magnesium alloys maraging steel martensitic stainless steel metallographic analysis metalworking...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006785
EISBN: 978-1-62708-295-2
... and residential plumbing systems, SCC can occur in brass plumbing components that are used in a hard temper condition or that have residual stresses from final finishing, such as rolled threads. Stainless steel clamps used in residential cross-linked polyethylene (PEX) plumbing systems exhibit SCC when moisture...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006760
EISBN: 978-1-62708-295-2
... that develops in ferritic and austenitic stainless steels after extensive exposure to temperatures ranging from 650 to 900 °C (1200 to 1650 °F). It forms more rapidly from ferrite than from austenite. Electrolytic etching with potassium hydroxide (KOH) reveals a sigma phase ( Fig. 26 ). Fig. 26 Duplex...
Book Chapter

Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003548
EISBN: 978-1-62708-180-1
... aluminum alone normally is not polarized to its pitting potential. In many environments, aluminum can be used in contact with chromium or stainless steels with only slight acceleration of corrosion; chromium and stainless steels are easily polarized cathodically in mild environments, so...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006783
EISBN: 978-1-62708-295-2
... these conditions. Corrosion of aluminum in contact with more cathodic metals is much less severe in solutions of most nonhalide salts, in which aluminum alone normally is not polarized to its pitting potential. In many environments, aluminum can be used in contact with chromium or stainless steels with only...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001839
EISBN: 978-1-62708-241-9
... ferritic steels: duplex stainless steels (code 1600) , Sandia National Laboratories Report , Sep 2008 , pp. 1600 – 1601 2. Yagodzinskyy Y. , Todoshchenko O. , Papula S. , Hänninen H. , Steel Res. Int . 82 ( 1 ), 20 ( 2011 ) 10.1002/srin.201000227 3. Louthan...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001818
EISBN: 978-1-62708-180-1
... of carbon steel for alloy or stainless steel, or vice versa ( Ref 1 ). Summary of statistics on pressure vessel failures compiled from 1981 through 1984 by the National Board of Boiler and Pressure Vessel Inspectors Table 1 Summary of statistics on pressure vessel failures compiled from 1981 through...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006808
EISBN: 978-1-62708-329-4
... can be seen in the lower right; black areas in the upper left are voids where ferrite has been attacked. Electrolytically etched with 10% ammonium persulfate. Original magnification: 500×. Source: Ref 63 Fig. 49 Duplex stainless steel 2205 weld showing stress-corrosion crack on the inside...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006816
EISBN: 978-1-62708-329-4
... and material factors that cause a part to fail during heat treatment. The article discusses the problems associated with heating and furnaces, quenching media, quenching stresses, hardenability, tempering, carburizing, carbonitriding, and nitriding as well as potential stainless steel problems and problems...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006778
EISBN: 978-1-62708-295-2
... sufficient to fracture the screws in ductile overload. Example 2: Forming Cracks on Stainless Steel Wire. Cold-drawn 6.4 mm (0.25 in.) diameter type 303 stainless steel wire sections failed during a forming operation. All wires failed at a gradual 90° bend. Investigation High-magnification...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006835
EISBN: 978-1-62708-329-4
... structure with uniform grain structure. Nonuniform strain rates can produce an unrecrystallized duplex structure, which, if undetected, can impact the part properties. Sonic inspection and metallographic inspection of the billet is used to determine this condition. Titanium, like aluminum, has a strong...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006812
EISBN: 978-1-62708-329-4
... to 3% of the total items to be carbon steel. A survey of equipment that required 320,000 individual instrument readings found that 1.8% of the material was supplied incorrectly, and the most frequent error was substitution of carbon steel for alloy or stainless steel, or vice versa ( Ref 1 ). Summary...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003543
EISBN: 978-1-62708-180-1
.... Example 2: Forming Cracks on Stainless Steel Wire Cold-drawn type 303 stainless steel wire sections, 6.4 mm (0.25 in.) in diameter, failed during a forming operation. All of the wires failed at a gradual 90° bend. Investigation High-magnification visual examination disclosed many fine ruptures...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003517
EISBN: 978-1-62708-180-1
... the structures in these two areas, the degree of service aging can be identified. The diameter of the particles should be measured to determine the amount of particle growth that has occurred. In alloys with duplex gamma-prime microstructures...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.9781627083294
EISBN: 978-1-62708-329-4
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003508
EISBN: 978-1-62708-180-1
... casting gray cast iron low-alloy steel malleable irons pressure die casting semisolid casting squeeze casting FAILURES OF CASTINGS, like the failures of wrought materials, can occur from service conditions, improper design and/or materials selection, manufacturing deficiencies, or a combination...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006831
EISBN: 978-1-62708-329-4
... Intergranular corrosion. (a) Sample from a cast stainless steel neck fitting. (b) Region adjacent to the intergranular corrosion revealing extensive σ-phase precipitation at grain boundaries; electrolytic etching using 10 N KOH. (c) Same area as (b) after repolishing and etching with Murakami’s reagent...