Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.steel.c9001532
EISBN: 978-1-62708-232-7
...Abstract Abstract Work rolls made of indefinite chill double-poured (ICDP) iron are commonly used in the finishing trains of hot-strip mills (HSMs). In actual service, spalling, apart from other surface degeneration modes, constitutes a major mechanism of premature roll failures. Although...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.conag.c0047352
EISBN: 978-1-62708-221-1
... iron. The two broken liners were sand blasted for visual inspection and subsequent metallography and hardness testing. Many cracks were found externally and on the undersides. There were also signs of mechanical damage that occurred inside the mill before detection of the failures. The underside...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.marine.c9001523
EISBN: 978-1-62708-227-3
... initiated from the tip of the cloverleaf pattern in >300 cases aboard several cargo vessels in various stages of construction. Consultants who analyzed the situation concluded that the problem may have been corrosion and hydrogen embrittlement. Three possible mechanisms of failure were considered...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.mech.c0048273
EISBN: 978-1-62708-225-9
...Abstract Abstract Several teeth of a bevel pinion which was part of a drive unit in an edging mill failed after three months in service. Specifications required that the pinion be made from a 2317 steel forging and that the teeth be carburized and hardened to a case hardness of 56 HRC...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.pulp.c9001650
EISBN: 978-1-62708-230-3
...Abstract Abstract Several air heat exchangers failed in service in a pulp and paper operation. The tubes were made from AISI 316 stainless steel with an extruded aluminum fin mechanically bonded to the outside. Originally, the failures were blamed on poor tube to header welds. The units were...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001055
EISBN: 978-1-62708-214-3
..., SEM fractographic, metallographic, chemical, and mechanical property (tension and impact toughness) analyses were conducted. On the basis of the tests and observations, it was concluded that the failure was the combined result of poor notch toughness (impact) properties of the steel, high stresses...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.machtools.c0091853
EISBN: 978-1-62708-223-5
...Abstract Abstract A 230 mm (9 in.) diameter disk attrition mill was scheduled to grind 6.35 mm (0.25 in.) diameter quartz particles to a 0.075 mm (0.003 in.) diameter powder. Due to severe wear on the grinding plates, however, the unit was unable to complete the task of grinding the rock...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001822
EISBN: 978-1-62708-241-9
..., and the presence of fatigue striations all supported transit fatigue as the damage mechanism. spiral welded pipe fracture transit fatigue HSLA steel longitudinal crack magnetic particle testing cyclic hoop stress API 5L-X65 (high-strength low-alloy plate steel) Introduction Failure Analysis...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001849
EISBN: 978-1-62708-241-9
... rolls and often leads to serious damage to the mill. Spalling is related to the thermal and mechanical stresses applied to the roll during service and is an indication of abnormal mill operation and/or poor material quality (e.g., impurity content, improper heat treatment). The effect of roll...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.steel.c9001535
EISBN: 978-1-62708-232-7
... Types , The Metals Society , 1979 , p 163 – 169 6. Sendzimir M.G. , Sendzimir Mills and their Rolls , 31st Mechanical Working and Steel Processing Conference Proceedings , Vol XXVII , The Iron and Steel Society , 1990 , p 329 – 334 7. Gulayev A. , High-Speed Steels...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001546
EISBN: 978-1-62708-217-4
... material, and those that exhibited a dual failure. The last category failed in the adhesive bond and also showed a type of pitting on one face of the base material. In a third case, a 2024-T4 extrusion section was found to exhibit blistering after chemical milling. The presence of interconnecting...
Book Chapter

Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006790
EISBN: 978-1-62708-295-2
...Abstract Abstract Engineered components fail predominantly in four major ways: fracture, corrosion, wear, and undesirable deformation (i.e., distortion). Typical fracture mechanisms feature rapid crack growth by ductile or brittle cracking; more progressive (subcritical) forms involve crack...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003560
EISBN: 978-1-62708-180-1
... sequence Step 1: Determine prior history Review documentary evidence  Test certificates  Mechanical/wear test data  Pertinent specifications  Correspondence  Interviews  Depositions and interrogatories Review service parameters  Design or intended operating parameters  Actual service conditions...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c0046227
EISBN: 978-1-62708-217-4
... and severity of pitting on the chemically milled surfaces and on the land surfaces, which were not chemically milled. Optical microscopic examination of the stripped sections revealed extensive pitting on both sides of the floors, including the chemically milled radii, which were mechanically machined after...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001609
EISBN: 978-1-62708-229-7
..., Specification for Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service , American Society of Mechanical Engineers , New York, NY , 2001 . 8. Anon. : ASTM A 763, Standard Practices for Detecting Susceptibility to Intergranular Attack in Ferritic Stainless Steels...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006806
EISBN: 978-1-62708-329-4
...Abstract Abstract A mechanical part, which supports the moving part, is termed a mechanical bearing and can be classified into rolling (ball or roller) bearings and sliding bearings. This article discusses the failures of sliding bearings. It first describes the geometry of sliding bearings...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.usage.c9001608
EISBN: 978-1-62708-236-5
..., with the resulting humidity causing corrosion that lifted the mill scale. Significant factors and mechanisms applying to corrosion of hot rolled steel stored outdoors in the tropics are as follows: Tropical countries tend to have high rainfalls, but the proportion of time it is raining can be low...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003567
EISBN: 978-1-62708-180-1
... Fig. 2 Ball mill liner plates. (a) New condition, before installation. (b) Worn condition, with partially worn grinding belt Fig. 3 Worn cone crusher liner after three months of use Fig. 8 Streamlines for water in pipe of variable diameter. Source: Ref 24 Fig. 1...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001730
EISBN: 978-1-62708-229-7
.... Fig. 1 This is a sectional view of the central shaft of a coal pulverizer which failed twice at the indicated area before the mill had to be shut down. The first crack went through the shaft, but it was rewelded by friction due to the spring pressure and the weight of grinding mechanism. When...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006826
EISBN: 978-1-62708-329-4
... integrity. The undesired twinning may reduce mechanical properties and fracture the machined part during high-stress part applications. A production schedule of a maximum number of roughing and finishing passes reduces the amount and depth of the twinning network. Chemical etching, chemical milling...