1-20 of 255 Search Results for

hydrogen-damage failures

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.mech.c0091475
EISBN: 978-1-62708-225-9
... (visual inspection and 2400x/6600x TEM analysis) supported the conclusion that failure was caused by hydrogen embrittlement, not SCC as might have been suspected. No recommendations were made. Cleavage Fractographs Stress corrosion cracking 431 UNS S43100 Hydrogen damage and embrittlement...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006784
EISBN: 978-1-62708-295-2
... of hydrogen damage in all the major commercial alloy systems. It covers the broader topic of hydrogen damage, which can be quite complex and technical in nature. The article focuses on failure analysis where hydrogen embrittlement of a steel component is suspected. It provides practical advice for the failure...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001613
EISBN: 978-1-62708-235-8
... coalescence in the center. The improper baking after electroplating of the screw led to H2-induced blistering/cracking. The high strength of the threaded region of the adjusting screw increased the failure propensity. Electroplating 16MnCr5 DIN 17210 Hydrogen damage and embrittlement Surface...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003552
EISBN: 978-1-62708-180-1
... is an overview of the different types of hydrogen damage in all the major commercial alloy systems. These two sections cover the broader topic of hydrogen damage, which can be quite complex and technical in nature. The third part of this article focuses on failure analysis where hydrogen embrittlement...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001277
EISBN: 978-1-62708-215-0
... • French D.N. , Failures of Boilers and Related Equipment , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 1986 , p 602 – 627 10.31399/asm.hb.v11.a0001816 • Hydrogen Damage and Embrittlement , Failure Analysis and Prevention , Vol 11 , ASM Handbook...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001746
EISBN: 978-1-62708-217-4
... Abstract Brittle intergranular fracture, typical of a hydrogen-induced delayed failure, caused the failure of an AISI 4340 Cr-Mo-Ni landing gear beam. Corrosion resulting from protective coating damage released nascent hydrogen, which diffused into the steel under the influence of sustained...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001839
EISBN: 978-1-62708-241-9
..., the failure is being attributed to hydrogen-induced damage. Potential sources of hydrogen are considered as are remedial measures for controlling hydrogen content in steels. References References 1. Zelinski J.A. , San Marchi C. , Technical reference on hydrogen compatibility...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001293
EISBN: 978-1-62708-215-0
.../asm.hb.v11.a0003544 • Hydrogen Damage and Embrittlement , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 809 – 822 10.31399/asm.hb.v11.a0003552 • Warke W. R. , Stress-Corrosion Cracking , Failure Analysis and Prevention , Vol 11 , ASM...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001739
EISBN: 978-1-62708-215-0
.... , Failures of Boilers and Related Equipment , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 1986 , p 602 – 627 10.31399/asm.hb.v11.a0001816 • Hydrogen Damage and Embrittlement , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001331
EISBN: 978-1-62708-215-0
... of pipe material was considered to be a contributing factor. Position of the pipe within the system caused the localized damage. Selected Reference Selected Reference • Hydrogen Damage and Embrittlement, Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c0048309
EISBN: 978-1-62708-229-7
...) Decarburizing Carbon Steel Hydrogen damage and embrittlement A 75-mm (3-in.) outside-diameter × 7.4-mm (0.290-in.) wall thickness carbon steel boiler tube ruptured as shown in Fig. 1 . The fracture was of the brittle window type, without the fishmouth appearance characteristic of overheating failures...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001113
EISBN: 978-1-62708-214-3
... International , 2002 , p 156 – 191 10.31399/asm.hb.v11.a0003509 • Hydrogen Damage and Embrittlement , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 809 – 822 10.31399/asm.hb.v11.a0003552 Remedial Action How Failure Could Have Been Prevented...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001802
EISBN: 978-1-62708-241-9
... , ASM Handbook , ASM International , 1990 , p 897 – 902 . 10.31399/asm.hb.v02.a0001100 Experimental Torsional Overload Introduction Tensile Overload Compressive Damage Hydrogen Embrittlement Fatigue Conclusions Kinking Failures NiTi wires were intentionally...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.conag.c0047474
EISBN: 978-1-62708-221-1
... 10.31399/asm.hb.v11.a0003508 • Lund R.A. and Sheybany S. , Fatigue Fracture Appearances , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 627 – 640 10.31399/asm.hb.v11.a0003539 • Hydrogen Damage and Embrittlement , Failure Analysis...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001540
EISBN: 978-1-62708-217-4
... overhaul. The specific source of hydrogen which produced failure was not ascertainable. Aircraft components Chromium plating Cylinders Landing gear 4340 UNS G43400 Intergranular fracture Hydrogen damage and embrittlement Introduction Ground maintenance personnel discovered hydraulic...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001731
EISBN: 978-1-62708-217-4
... during overhaul. Sometime prior to the final failure small intergranular cracks caused by hydrogen embrittlement or stress-corrosion, were formed in the damaged area. The fact that the surface damage was at the parting line of the forging may have contributed to the cause of the failure as this area...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001322
EISBN: 978-1-62708-215-0
... Ibbes in Power Plants,” Br Corros. J. , Vol. 16 , 1981 , p 25 – 31 . Selected Reference Selected Reference • Hydrogen Damage and Embrittlement , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 809 – 822 10.31399/asm.hb.v11.a0003552...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c0048630
EISBN: 978-1-62708-217-4
... was specified for a sample quantity of bolts from each lot. Electroplating Hydrogen embrittlement Cadmium-plated steel Surface treatment related failures Hydrogen damage and embrittlement Two clevis-head self-retaining bolts used in the throttle-control linkage of a naval aircraft failed...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001546
EISBN: 978-1-62708-217-4
... Laboratory Report No. NLR TR76065 U, 5 September 1976 . Selected Reference Selected Reference • Fatigue Failures , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 700 – 727 10.31399/asm.hb.v11.a0003544 • Hydrogen Damage and Embrittlement...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.homegoods.c0048674
EISBN: 978-1-62708-222-8
... structure and the method of plating the fastener with zinc was changed from electroplating to a mechanical deposition process to thus avoid hydrogen embrittlement. Fasteners, corrosion Electroplating Lawn furniture 1060 UNS G10600 Surface treatment related failures Hydrogen damage...