1-20 of 41 Search Results for

graphite nucleation

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001337
EISBN: 978-1-62708-215-0
... regions examined. It was concluded that preferential nucleations of graphite nodules in a series of bands weakened the steel locally, producing preferred fracture paths. Formation of these graphite bands probably expedited the creep failure of the tube. Future failures may be avoided by using low-alloy...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001813
EISBN: 978-1-62708-241-9
... analysis distribution of graphite nodules low alloy steel (low alloy steel, general) carbon steel (carbon steel, general) Introduction Nucleation and Growth of Graphite Industrial Cases Discussion Conclusions References References 1. Wilson J.G. : Graphitization of steel...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.conag.c9001200
EISBN: 978-1-62708-221-1
...Abstract Abstract During the operation of tractors with cantilevered body, the lateral wall of the hypoeutectic cast iron cylinder blocks cracked repeatedly. Three of the blocks were examined. The grain structure of the thick-walled part consisted of uniformly distributed graphite of medium...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006793
EISBN: 978-1-62708-295-2
... on the Impact Wear Resistance of Compacted Graphite Iron (CGI) , Wear , Vol 270 , 2011 , p 302 – 311 10.1016/j.wear.2010.11.003 37. Slatter T. , Lewis R. , and Jones A.H. , The Influence of Cryogenic Processing on Wear on the Impact Wear Resistance of Low Carbon Steel and Lamellar...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006778
EISBN: 978-1-62708-295-2
... failure analysis or incomplete root-cause investigation can be very misleading or even dangerous. Ductile fracture occurs from the nucleation, growth, and coalescence of microvoids during deformation. Second-phase particles and inclusions typically provide the nucleation sites for initiation...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003543
EISBN: 978-1-62708-180-1
... the nucleation, growth, and coalescence of microvoids during deformation. Second-phase particles or inclusions typically provide the nucleation sites for initiation of the microvoids, which then grow and coalesce as deformation progresses further. Ductile fracture by void growth and coalescence can occur by two...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003545
EISBN: 978-1-62708-180-1
... graphitization that occurs in iron-base alloys without adequate carbide stabilizing elements present. Iron carbide (cementite) decomposes to graphite and iron. Normally, chromium is added to prevent this. In situ graphitization is also affected strongly by molybdenum content and deoxidation practice. The extent...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006780
EISBN: 978-1-62708-295-2
... initially nucleate during creep deformation and then grow. A distinct correlation exists for these data, such that a minimum and maximum remaining life fraction can be specified ( Table 3 ). The presence of detrimental microstructural features, including sigma phase and graphitization, can also be monitored...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003508
EISBN: 978-1-62708-180-1
... causing a localized seam Oxide inclusion or skins, seams G 143 (a) Folded films of graphitic luster in the wall of the casting Lustrous carbon films, or kish tracks G 144 Hard inclusions in permanent molded and die cast aluminum alloys Hard spots (a) Defects that under some...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006775
EISBN: 978-1-62708-295-2
...Abstract Abstract This article focuses on characterizing the fracture-surface appearance at the microscale and contains some discussion on both crack nucleation and propagation mechanisms that cause the fracture appearance. It begins with a discussion on microscale models and mechanisms...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003538
EISBN: 978-1-62708-180-1
... concepts. bending brittle fracture compression failure deformation ductile crack nucleation ductile fracture ductility fractography manufacturing imperfections metals microvoid coalescence notched specimen plastic flow root cause failure analysis single-crystal cleavage models specimen...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.steel.c9001598
EISBN: 978-1-62708-232-7
... at these temperatures. If void nucleation is restricted to the grain boundaries, the observation of voids within the grains demonstrates that the voids did not effectively pin the boundary. Mechanical properties, such as creep resistance and mechanical strength, are influenced by grain size. At room temperature...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006831
EISBN: 978-1-62708-329-4
... of oxide skins, most often causing a localized seam Oxide inclusion or skins, seams G 143 (a) Folded films of graphitic luster in the wall of the casting Lustrous carbon films, or kish tracks G 144 Hard inclusions in permanent molded and die cast aluminum alloys Hard spots...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.marine.c9001003
EISBN: 978-1-62708-227-3
... by high heat flux. The embrittlement was shown to be caused by the flow of corrosion generated hydrogen which converted the cementite to methane which nucleated voids in the steel. A thermodynamic estimate indicated that a small amount of chromium would stabilize the carbides against decomposition...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003555
EISBN: 978-1-62708-180-1
... and overall wastage of stainless steels, with or without an oxidizing environment ( Ref 9 , 10 ). Corrosion products in the pits consist of metal carbides, metal oxides, and graphite. The attack is localized, and carburization is confined to the pit. Slight modifications in the process conditions may...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003540
EISBN: 978-1-62708-180-1
...-nitrided layer of ductile iron (ASTM 80-55-06), (b) transgranular fracture by cleavage in ductile iron (ASTM 80-55-06), and (c) ductile fracture with equiaxed dimples from microvoid coalescence around graphite nodules in a ductile iron (ASTM 65-40-10). Picture widths are approximately 0.2 mm (0.008...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006787
EISBN: 978-1-62708-295-2
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001816
EISBN: 978-1-62708-180-1
... of film boiling on tube-wall temperature appears as sharp breaks in the curves for moderate, high, and very high heat fluxes in Fig. 5 . With increasing heat flux, the onset of unstable film boiling, also known as departure from nucleate boiling (DNB), occurs at lower steam qualities, and tube-wall...
Book Chapter

Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003544
EISBN: 978-1-62708-180-1
... to a better understanding of both crack nucleation in regions of localized strain and the subsequent crack growth mechanisms outside the plastic zone in the qualification of component designs or to conduct failure analyses. Infinite-Life Criterion (<italic>S</italic>-<italic>N</italic> Curves) The safe...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006777
EISBN: 978-1-62708-295-2
... Fig. 1 Scanning electron microscopy images of (a) intergranular fracture in ion-nitrided layer of ductile iron (ASTM 80-55-06), (b) transgranular fracture by cleavage in ductile iron (ASTM 80-55-06), and (c) ductile fracture with equiaxed dimples from microvoid coalescence around graphite...