1-20 of 64 Search Results for

galvanized coating

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001099
EISBN: 978-1-62708-214-3
... fasteners and appropriately-applied and treated compatible coatings. Brittle fracture Castings Diffusers Galvanic corrosion Transition joints 356.0 UNS A03560 Hydrogen damage and embrittlement Galvanic corrosion Background Uncoated high-strength alloy steel cap screws retaining a cast...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.bldgs.c9001219
EISBN: 978-1-62708-219-8
...Abstract Abstract During construction of a river bridge with 80 twisted cables, one or more fractures were found in each of 21 wires of 18 cables before assembly. All were located at the outside wrapping whose Z-profile wires were galvanically zinc-coated. It was suspected that hydrogen played...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001100
EISBN: 978-1-62708-214-3
... of the bolts were gray and nonreflective, typical of a hot-dip galvanized coating. The long leg of the as-fractured bolt extended 448 mm (17.6 in.) from the bend area. The short leg extended 67 mm (2.6 in.) from the bend. The diameter of unthreaded leg regions was measured to be 18 mm (0.7 in.). The small...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003549
EISBN: 978-1-62708-180-1
...: change in the environment; change in the alloy or heat treatment; change in design; use of galvanic protection; use of inhibitors; use of nonmetallic coatings and liners; application of metallic coatings; use of surface treatments, thermal spray, or other surface modifications; corrosion monitoring...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.homegoods.c0006897
EISBN: 978-1-62708-222-8
...Abstract Abstract The small cable (drop wire) providing service for individual subscribers from the aerial plant is held in place by a clamp made of a tin-coated brass body (attached to the cable) and a copper tail wire loop (attached to a galvanized steel hook or to a porcelain insulator...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001030
EISBN: 978-1-62708-214-3
...Abstract Abstract Cracks were discovered between interference-fit fasteners (MoS2-coated Ti-6Al-4V) that had been incorporated into a fighter aircraft primary structural frame (D6ac steel) to enhance structural fatigue life. Examination of sections cut from the cracked frame established...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.bldgs.c9001656
EISBN: 978-1-62708-219-8
... subjected to sinusoidal load fluctuations at 6.7 Hz in air, 3% NaCl solution, and natural sea water are described. Reinforcement types studied included: hot-rolled mild steel bar, hot-rolled alloyed high strength bar, cold-worked high strength bar, galvanized bar of all these three types, nickel-clad bar...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c9001745
EISBN: 978-1-62708-217-4
... by galvanic action between aluminum alloy bracket and steel bolt. To preclude or minimize recurrences, fittings in service should be inspected periodically by dye penetrant for signs of cracking on the end face and within the fitting hole and protected with a suitable coating to exclude damaging chlorides...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c0046535
EISBN: 978-1-62708-234-1
... depression in the backfill revealed the site of failure. Analysis (visual inspection, electrical conductivity, and soil analysis) supported the conclusions that the failure had resulted from galvanic corrosion at a point where the corrosivity of the soil was substantially greater than the average, resulting...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001808
EISBN: 978-1-62708-241-9
... the bottom of the pipe, but the attack was localized corrosion not general corrosion. Furthermore, the galvanized coating was uniform in the un-corroded areas. Due to the stagnant conditions and lack of fresh water and oxygen, oxygen corrosion was rejected as the likely corrosion mechanism. MIC...
Book Chapter

Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003548
EISBN: 978-1-62708-180-1
... in protective coatings may lead to severe galvanic corrosion in the localized region of the coating imperfection. It is extremely dangerous to coat the anodic member of a couple because this may only reduce its active area, which severely accelerates the attack at these holidays in the otherwise protective...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001817
EISBN: 978-1-62708-241-9
... such as decarburized layer, nonmetallic inclusions, or martensite formation. In addition, the wires were free from any sort of corrosion and pitting. Therefore, corrosion had no role in the failure of wires. This was due to the zinc coating of wires, where in the galvanic couple of iron–zinc, even a loss of a portion...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006783
EISBN: 978-1-62708-295-2
... in protective coatings may lead to severe galvanic corrosion in the localized region of the coating imperfection. It is extremely dangerous to coat the anodic member of a couple because this may only reduce its active area, which severely accelerates the attack at these holidays in the otherwise protective...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001812
EISBN: 978-1-62708-180-1
... on stress-corrosion cracking, hydrogen embrittlement, and liquid-metal embrittlement of bolts and nuts. The article explains the most commonly used protective metal coatings for ferrous metal fasteners. Zinc, cadmium, and aluminum are commonly used for such coatings. The article also illustrates...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003520
EISBN: 978-1-62708-180-1
... turned, pickled, and hot dip galvanized. A tool steel slip ring was placed under the head between the pin and the insulator. Misalignment caused the tool steel ring to make marks in the galvanized coating on one side where it was in compression but not elsewhere, because there was no contact...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001215
EISBN: 978-1-62708-235-8
... alloy formation. Even in the case of steel parts with lower silicon contents the reaction between iron and zinc can continue until the pure zinc layer has been consumed entirely if the work piece is not cooled sufficiently after withdrawal. Coating defects Galvanized steels Hot dip galvanizing...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001832
EISBN: 978-1-62708-241-9
... using galvanized 1 16 in. steel sheet. Visual inspection revealed a high integrity weld. However, observation of a sharp definition of the weld across the plate thickness suggested that the weld temperature was relatively high. The zinc coating had been removed on both edges prior...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006794
EISBN: 978-1-62708-295-2
... of Mines , https://www.cdc.gov/niosh/mining/content/history.html 2. NRS Galvanized Brake Pads , Toronto , Canada , https://nrsbrakes.com/galvanized-steel-brake-pads/ 3. Rigney D.A. , Sliding Wear of Metals , Ann. Rev. Mater. Sci. , Vol 18 , 1988 , p 141 – 163 10.1146/annurev.ms...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001695
EISBN: 978-1-62708-229-7
... concentrations). Galvanic couple between stainless steel bucket/hanger and aluminum fuel. Galvanic couple between aluminum and uranium. Scratches and imperfections in protective oxide coating on the cladding Relatively stagnant water. The galvanic couple between the stainless steel...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001812
EISBN: 978-1-62708-241-9
... are not aware of these potential sources and the dangers involved. Some sources of embrittling metal environments in industry Table 1 Some sources of embrittling metal environments in industry Coatings, e.g., Cd, Zn on steels, inadvertently exposed to high temperatures Solders, Brazes...