1-20 of 134 Search Results for

forging equipment

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001362
EISBN: 978-1-62708-215-0
...Abstract Abstract Numerous cracks observed on the surface of a forged A470 Class 4 alloy steel steam turbine rotor disc from an air compressor in a nitric acid plant were found to be the result of caustic induced stress-corrosion cracking (SCC). No material defects or anomalies were observed...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001761
EISBN: 978-1-62708-241-9
...Abstract Abstract An investigation of a damaged crankshaft from a horizontal, six-cylinder, in-line diesel engine of a public bus was conducted after several failure cases were reported by the bus company. All crankshafts were made from forged and nitrided steel. Each crankshaft was sent...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001811
EISBN: 978-1-62708-180-1
... as that of the failed part, fabrication practice (machining, welding, forging, or casting), heat treatment, types of loading to which the equipment is subjected, and operating environment, such as corrosive or high-temperature atmospheres. Many failures may be the result of a combination of several faults...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006830
EISBN: 978-1-62708-329-4
... Fabrication practice (machining, welding, forging, or casting) Heat treatment Types of loading to which the equipment is subjected Operating environment, such as corrosive or high-temperature atmospheres Failures may be the result of a combination of several faults or contributing factors...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001845
EISBN: 978-1-62708-241-9
.... The investigation results suggest that the root cause of failure was a forging lap that occurred during manufacturing. Precracks induced by the forging defect and the influence of preload stress (due to bolt torque) caused the premature failure. cable clamps brittle fracture forging overlap copper alloy...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.matlhand.c9001262
EISBN: 978-1-62708-224-2
... probable that the real damage was done during the heat-up forging (drop-forging) and could not be removed during heat-treatment. Chains Cracking (fracturing) Drop forgings Overheating 30CrMoV 9 Metalworking-related failures A chain link which was part of the hoisting mechanism of a drop...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006802
EISBN: 978-1-62708-329-4
...Abstract Abstract Life assessment of structural components is used to avoid catastrophic failures and to maintain safe and reliable functioning of equipment. The failure investigator's input is essential for the meaningful life assessment of structural components. This article provides...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003512
EISBN: 978-1-62708-180-1
... inspection stress structural components structural design LIFE ASSESSMENT of structural components is used to avoid catastrophic failures and to maintain safe and reliable functioning of equipment. The articles in the “Structural Life Assessment Methods” Section in this Volume are written to provide...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001005
EISBN: 978-1-62708-215-0
... HB, revealed that fatigue crack initiation occurred from the tip of oxide scale inclusions forged into the U-shaped arm at the inside radius. Corrective action involved redesigning the steering arm to increase the minimum forging radius and reduce the stress level at the inner-bend radius...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003500
EISBN: 978-1-62708-180-1
... broadly, from maintenance training issues, to marginal equipment reliability, to business systems conflicts, to policy inconsistencies, to poor working conditions on the shop floor. When a problem occurs, the responsible organization will analyze the problem to determine the cause and solve it. However...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006753
EISBN: 978-1-62708-295-2
... to manufacture at normal production rates … Material discontinuities that cause failures in metal products Table 2 Material discontinuities that cause failures in metal products Metal product form Types of discontinuities Forgings Laps Bursts Cracks Flow-through defects Extrusion-type...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001818
EISBN: 978-1-62708-180-1
...-processing plants are discussed in this article. These types of equipment operate over a wide range of pressures and temperatures and are exposed to a wide variety of operating environments. The National Board of Pressure Vessel Inspectors compiles domestic statistics on reported accidents involving...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006812
EISBN: 978-1-62708-329-4
... pressure vessels refineries PRESSURE VESSELS, PIPING, and associated pressure-boundary items of the types used in nuclear and conventional power plants, refineries, and chemical-processing plants are discussed in this article. These types of equipment operate over a wide range of pressures...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.rail.c9001450
EISBN: 978-1-62708-231-0
... that was equipped with an automatic control to maintain the air-gas ratio at such a value that reducing conditions were obviated. It was also stated that the rivets had been inserted from the fireside, therefore the original heads would be on that side of the box. Microscopical examination revealed that while...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001079
EISBN: 978-1-62708-214-3
.... The material was found to be a typical Cr-Mo-V steel, and it met the property requirements. No evidence of temper embrittlement was found. The analyses showed that the observed flaws were present in the original forging and attributed them to lack of ingot consolidation. A series of actions, including...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001039
EISBN: 978-1-62708-214-3
...Abstract Abstract The 4140 steel steering spindle on a tricycle agricultural field chemical applicator failed, causing the loss of the front wheel and overturn of the vehicle. The spindle was a solid 120 mm (4.75 in.) diam forging. It had been machined to 115 mm (4.5 in.) in diameter to fit...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003553
EISBN: 978-1-62708-180-1
... rolled, extruded, or forged products are stressed in the short-transverse direction. In wrought austenitic stainless steels, crack paths are usually transgranular if proper heat treatment has been employed. However, if thermal processing has produced sensitization because of carbide precipitation...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.9781627083294
EISBN: 978-1-62708-329-4
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006761
EISBN: 978-1-62708-295-2
... by the environment and/or temperature of the service conditions. The systems, methodologies, equipment, environment, and human factors that can affect variability in mechanical testing can be illustrated in a fish-bone diagram ( Fig. 1 ). Fig. 1 Fish-bone diagram showing the systems, methodologies, equipment...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001536
EISBN: 978-1-62708-229-7
... a matter of removing these surface deposits. Component decontamination is desirable both from the standpoints of reducing personnel exposure to radiation and of reducing the likelihood of subsequent contamination of laboratory space and equipment. In failure analysis, the need to decontaminate the failed...