1-20 of 95 Search Results for

creep-rupture life

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c9001738
EISBN: 978-1-62708-220-4
..., the oxidation-cracks stopped. To determine the residual creep life of the sound (non-cracked) bottom manifold material, iso-stress creep tests were performed. It was found that tertiary creep started at 7% strain. The time-to-rupture was greater than 100,000 h. It was concluded that the bottom manifold...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001011
EISBN: 978-1-62708-229-7
... that the process of creep was not operative throughout the life of the equipment. Outlet tubes Overheating Oxidation Superheaters 2.25Cr-1Mo Creep fracture/stress rupture Thermal fatigue fracture After some 87,000 h of operation, failure took place in the bend of a steam pipe connecting a coil...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001004
EISBN: 978-1-62708-229-7
... with a miniature sample sampling method, represents an attractive approach to the toughness assessment of critical power plant components. Grain boundaries Phosphorus Segregation Stream turbines Studs Temper embrittlement 1CrMoV Creep fracture/stress rupture Introduction Creep-Reverse Temper...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003545
EISBN: 978-1-62708-180-1
... stresses. Source: Ref 10 Fig. 6 Logarithmic plot of stress-rupture stress versus rupture life for Co-Cr-Ni-base alloy S-590. The significance of inflection points A, B, N, O, and Y is explained in the text. Source: Ref 10 Fig. 4 Typical creep deformation and intergranular cracking...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006780
EISBN: 978-1-62708-295-2
... for nickel. Source: Ref 21 Fig. 15 Logarithmic plot of stress-rupture stress versus rupture life for nickel-base alloy U-700 at 815 °C (1500 °F). The increasing slope of the curve to the right of the sigma break is caused by sigma-phase formation. Fig. 6 Creep life assessment based...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006807
EISBN: 978-1-62708-329-4
.../asm.hb.v08.9781627081764 7. Viswanathan R. , Damage Mechanisms and Life Assessment of High-Temperature Components , ASM International , 1989 10.31399/asm.tb.dmlahtc.9781627083409 8. Larson F.R. and Miller J. , A Time-Temperature Relationship for Rupture and Creep Stresses , Trans. Am...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003517
EISBN: 978-1-62708-180-1
..., microstructural evaluations, the creep cavitation damage assessment, the oxide-scale-based life prediction, and high-temperature crack growth methods. coating evaluation creep cavitation damage assessment elevated-temperature failure gas turbine blade hardness testing high-temperature crack growth...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001758
EISBN: 978-1-62708-241-9
... at carbides and other microconstituents, especially in single crystal castings that do not possess grain boundaries. gas turbine engine components creep deformation overheating nickel-base superalloy interdendritic stress-rupture fracture stress-rupture testing stress-rupture life Cast nickel...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001669
EISBN: 978-1-62708-229-7
... directly for evidence of microstructural damage. The base metal samples, in which it was not expected that damage could be detected by standard metallographic techniques [ 2 ], were intended for post-exposure creep-rupture tests to determine the amount of creep life expended during service exposure...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001279
EISBN: 978-1-62708-215-0
... thickness measured on ruptured ring section) The tube metal temperature was constant over the operating life of the tube The tube experienced about 8,000 hours of service each year A mean temperature of 528 °C (983 °F) was calculated to correspond to a creep life of about 13 years using...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001771
EISBN: 978-1-62708-241-9
... and creep of Ni–Cr–Fe alloys in carburizing and oxidizing environments . Oxid. Met. 12 ( 5 ), 387 – 404 ( 1978 ) 10.1007/BF00612086 10. Bennett M.J. , Price J.B. : A physical and chemical examination of an ethylene steam cracker coke and of the underlying pyrolysis tube . J. Mater...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c0060144
EISBN: 978-1-62708-234-1
... cell, each filled with a nickel catalyst. The tubes were centrifugally cast from ASTM A297, grade HK-40 (Fe-25Cr-20Ni-0.40C), heat-resistant alloy. The tube was concluded after metallurgical inspection to have failed from creep rupture (i.e., stress rupture). A project for detecting midwall creep...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c9001735
EISBN: 978-1-62708-220-4
... tube remaining life showed the welds to be inadequate, and to have a strength and creep resistance below those of the base metal. Reformer furnaces Tubine Welded joints HK-40 UNS J94224 Creep fracture/stress rupture A sample tube was removed from a reformer furnace for life assessment...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001711
EISBN: 978-1-62708-229-7
..., as a function of oxidation thickness, temperature and time, confirming the creep failure diagnostic. Boiler pipes Electric power generation Steam 10CrMo9-10 X20MoV12-1 Creep fracture/stress rupture Introduction Creep Failure in 10CrMo9-10 Steel Pipes Diagnostic Factors: Oxide Thickness...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006802
EISBN: 978-1-62708-329-4
...-welded high-energy piping failures ( Ref 13 ) 1986–2000 Cavitation and creep voids in welds, resulting in catastrophic high-energy rupture Development of elevated-temperature life assessment techniques for cavitation and creep failure Aloha incident, Boeing 737 ( Ref 14 ) 1988 Accelerated...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003512
EISBN: 978-1-62708-180-1
... of materials with improved toughness Seam-welded high-energy piping failures ( Ref 12 ) 1986–2000 Cavitation and creep voids in welds resulting in catastrophic high-energy rupture Development of elevated-temperature life assessment techniques for cavitation and creep failure Aloha Incident, Boeing 737...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.usage.c0048303
EISBN: 978-1-62708-236-5
... increased the actual operating stress. Tube wastage and high operating temperatures hastened the failure. A better understanding of the material condition of this superheater was recommended to verify all the suspect hot tubes. Overheating 2.25Cr-1Mo Creep fracture/stress rupture This example...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c9001737
EISBN: 978-1-62708-229-7
... that the casing could be welded successfully, it was suggested that the remaining useful life was effectively exhausted and that it should be replaced. Thermal stresses produced during operation would rapidly result in additional cracks. Casings Gas turbines Thermal stresses 321 UNS S32100 Creep...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c9001688
EISBN: 978-1-62708-234-1
... in each case. Decarburization Superheaters Tube components ASTM A209 Creep fracture/stress rupture Intergranular corrosion High-temperature corrosion and oxidation The authors have been involved in the examination of many failed superheater components and the two examples given here...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c0048845
EISBN: 978-1-62708-229-7
...Abstract Abstract The maximum life of base-loaded headers and piping is not possible to be predicted until they develop microcracking. The typical elements of a periodic inspection program after the occurrence of the crack was described extensively. Cracks caused by creep swelling in the stub...