1-20 of 560 Search Results for

composite metals

Sort by
Image
Published: 01 December 1992
Fig. 9 EDS scan of weld metal for constituents. Element Composition, % Iron 84.33 Chromium 13.68 Nickel 0.36 Silicon 0.35 Manganese 1.25 Molybdenum 0.03 More
Image
Published: 01 December 1992
Fig. 10 Composite optical micrograph of crack, which initiated in the weld metal and propagated into the base material. Etched with Vilella's reagent. More
Image
Published: 15 May 2022
Fig. 17 Rubber/metal composite More
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001128
EISBN: 978-1-62708-214-3
... steels. (a) Base metal. (b) Weld metal. Fig. 7 Microstructure of fusion line area. Chemical Analysis/Identification The chemical compositions of the base and weld metals are presented in Table 1 . Results of chemical analysis Table 1 Results of chemical analysis Elements...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003529
EISBN: 978-1-62708-180-1
... spectrometry, and wavelength-dispersive spectrometry. The article concludes with information on specimen handling. backscattered electron imaging economy test elemental composition analysis energy-dispersive spectrometry failure analysis metals microchemical analysis referee test specimen...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c0048767
EISBN: 978-1-62708-235-8
... were revealed at the edges of the weld metal. It was revealed by chemical analysis of this band that a stainless steel filler metal had been used which produced mixed composition at the weld boundaries. The plating material was revealed to be nickel by chemical analysis. It was concluded that clapper...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001049
EISBN: 978-1-62708-214-3
... in Table 1 . Composition of weld metal Table 1 Composition of weld metal Element Composition, % Section 1, near weld metal surface Section 2, near weld metal surface Proprietary Filler Metal Iron 52 40 1.0 Nickel 35 44 72.0 Chromium 9 11 20.0 Niobium 2 2 2.5...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.steel.c9001714
EISBN: 978-1-62708-232-7
... Abstract In a HyL III heat exchanger's radiant pipes, metal dusting reduced the pipe thickness from 8.5 to 3 mm in just nine months, leaving craters on the inner surface. The pipes are fabricated from HK 40 alloy. The heated gas (400 to 800 deg C) consisted of CO, CO2, and H2, with a 4:1 CO/CO2...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c9001534
EISBN: 978-1-62708-220-4
... specimens 3.7 Chemical Analysis Chemical compositions of the pipe, the dished end, and the weld metal are given in Table 2 . Carbon and sulfur contents of pipe and dished-end materials were determined by a combustion method, and a titrametric method was used to estimate the concentrations...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001829
EISBN: 978-1-62708-241-9
..., and filler metal are listed in Table 1 . Fig. 1 (a) First-stage vane and (b) inner root area of 700ES Chemical compositions of bond-coat layer, base, and filler metal Table 1 Chemical compositions of bond-coat layer, base, and filler metal Chemical Composition, wt.% Co Cr Ni W...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001085
EISBN: 978-1-62708-214-3
... scans of the material, as well as the approximate alloy constituents of both the base metal and the weld metal. The scans show that the casting was welded with a weld material similar in composition to the casting material, in accordance with specifications. Fig. 8 EDS scan of polished specimen...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001595
EISBN: 978-1-62708-235-8
... of alloying elements. A comparison measure, identified as the critical diameter(D I ), was implemented to estimate the hardening response of a steel from the chemical composition. The critical diameter calculated for a given steel composition can thereafter be used to create an approximate through-thickness...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001107
EISBN: 978-1-62708-214-3
... Abstract A 150 mm (6 in.) diam, 1.6 mm (0.065 in.) thick alloy 800 1iner from an internal bypass line in a hydrogen reformer was removed from a waste heat boiler because of severe metal loss. Visual and metallographic examinations of the liner indicated severe metal wastage on the inner surface...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.mech.c0048607
EISBN: 978-1-62708-225-9
... Abstract Stainless steel bolts broke after short-term exposure in boiler feed-pump applications. Specifications required that the bolts be made of a 12% Cr high-strength steel with a composition conforming to that of AISI type 410 stainless steel. Several bolts from three different...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001194
EISBN: 978-1-62708-235-8
... Abstract A seamless hot-drawn boiler tube NW 300 of 318 mm OD and 9 mm wall thickness made of steel 15Mo3 was bent with sand filling after preheating allegedly to 1000 deg C. In the process it had cracked repeatedly in the drawn fiber. The composition corresponded to specifications...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001836
EISBN: 978-1-62708-241-9
... along a crack on the extrados to document the crack morphology using optical microscopy. In addition to cracking, golden-yellow streaks were visible at the extrados, and the composition was examined using scanning electron microscopy with energy dispersive spectroscopy. Based on the results...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001331
EISBN: 978-1-62708-215-0
... time steam flowed through the length of pipe was during startup or shutdown procedures. A sealer compound (composition unknown) was periodically pumped into the steam to seal leaky valve stems in the system. Pertinent Specifications P22 low-alloy steel was specified for this application...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c0091533
EISBN: 978-1-62708-217-4
... with oxalic acid) supported the conclusion that the clamp fractured by SCC because the work metal was sensitized. Sensitization occurred during long-term exposure to the service temperature; the effects of sensitization were intensified as a result of cold forming. Recommendations included using a work metal...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001365
EISBN: 978-1-62708-215-0
... . The as-deposited weld filler metal composition is consistent with the nominal 12% Cr requirements. Chemical composition of the damaged impeller Table 1 Chemical composition of the damaged impeller Composition, wt% Chemical requirements for A743 grade CA-15 stainless steel Element Damaged...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001088
EISBN: 978-1-62708-214-3
... Abstract A 25 mm (1 in.) diam carrier shaft failed suddenly during operation. The shaft failed near the toe of the 4.8 mm (316 in.) frame-to-shaft 60 deg and 120 deg submerged metal arc (SMA) tack welds after an unknown time in service. Material specifications called for the shaft to be made...