1-20 of 84 Search Results for

cold forging

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003507
EISBN: 978-1-62708-180-1
..., and scabs. The article provides a discussion on the imperfections found in steel forgings. The problems encountered in sheet metal forming are also discussed. The article concludes with information on the causes of failure in cold formed parts. anisotropy blisters centerline shrinkage chemical...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c0047199
EISBN: 978-1-62708-234-1
... show conclusively that large changes in strength and exfoliation characteristics of 7075 forgings can be induced by changes in temperature or time of thermal treatment. With regard to the effect of quenching rate on exfoliation characteristics, a cold-water quench below 25 deg C (75 deg F) would appear...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001541
EISBN: 978-1-62708-235-8
... fractograph proved the crack to be a forging defect called a cold shut. Because defects of this type are usually detected when the raw forging is inspected, this occurrence was considered to be an isolated instance. Cold shuts Cracking (fracturing) Forgings 7075-T6 UNS A97075 Metalworking-related...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001359
EISBN: 978-1-62708-215-0
... investigation revealed that fused material from the blade had been thrown onto the cold blade surface during a grinding operation to remove the targeting bosses from the forgings, thereby causing local embrittlement. It was recommended that extreme care be taken during grinding operations to prevent the hot...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.auto.c0091893
EISBN: 978-1-62708-218-1
...Abstract Abstract An automotive front-wheel outer angular-contact ball bearing generated considerable noise shortly after delivery of the vehicle. The inner and outer rings were made of seamless cold-drawn 52100 steel tubing, the balls were forged from 52100 steel, and the retainer was stamped...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001815
EISBN: 978-1-62708-241-9
... in the material is unlikely. Preferential Hard Forged Plane A theory was presented by another involved party that a preferential hard plane of material may have been created during the cold-heading operation. This hard plane would have lower ductility and possibly separate at the grain boundaries under...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001788
EISBN: 978-1-62708-241-9
... on different failure concepts . J. Mater. Process. Technol. 80–81 , 602 – 607 ( 1998 ) 10.1016/S0924-0136(98)00168-X 6. Falk B. , Engel U. , Geiger M. : Fundamental aspects for the evaluation of the fatigue behavior of cold forging tools . J. Mater. Process. Technol. 119 ( 1–3...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c9001724
EISBN: 978-1-62708-234-1
... diameter, 3 in. thick and 21.25 in. long — cold working the ring requires very powerful machinery; in fact, special techniques had to be employed to achieve the required degree of cold working with the 4000-ton press at the forge plant of the steelmakers, Thos. Firth and John Brown, Ltd., of Sheffield...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001079
EISBN: 978-1-62708-214-3
.... During cold starts, the bore region also experiences a high tangential thermal stress in tension because of the high temperature gradient from the periphery to the bore. The materials used in turbine forgings (Ni-Mo-V, Cr-Mo-V, or Ni-Cr-Mo-V steels) are susceptible to temper embrittlement when...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001814
EISBN: 978-1-62708-180-1
... in cold-working and hot-working applications. It reviews problems introduced during mechanical design, materials selection, machining, heat treating, finish grinding, and tool and die operation. The brittle fracture of rehardened high-speed steels is also considered. Finally, failures due to seams or laps...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c0047830
EISBN: 978-1-62708-235-8
... initiated in the fold and was propagating across the cheek. Examination of a section through the fracture surface disclosed cold working of the surface, which could have been the result of a rather extended period of fatigue cracking. Chemical analysis of the two forgings found the metal to be 4140...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001811
EISBN: 978-1-62708-180-1
... as that of the failed part, fabrication practice (machining, welding, forging, or casting), heat treatment, types of loading to which the equipment is subjected, and operating environment, such as corrosive or high-temperature atmospheres. Many failures may be the result of a combination of several faults...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c9001252
EISBN: 978-1-62708-235-8
...Abstract Abstract An octagonal steel ingot weighing 13 tons made of manganese-molybdenum steel developed gaping cross-cracks on all eight sides in the forging press during initial pressure application. It was reported that the steel had been melted in a basic 12-ton arc furnace, oxygenated...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.steel.c9001535
EISBN: 978-1-62708-232-7
... References References 1. Manganello S.G. and Churba D.R. , Roll Failures and What to Do When They Occur , Iron Steelmaker , Vol 7 ( No. 12 ), 1980 , p 26 – 34 2. Mukherjee D. , Ray A. , and Bhattacharyya S.K. , Spalling Resistance of Forged Steel Cold Rolling...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001270
EISBN: 978-1-62708-215-0
...Abstract Abstract An investigation was conducted to determine the factors responsible for the occasional formation of cracks on the parting lines of medium plain carbon and low-alloy medium-carbon steel forgings. The cracks were present on as-forged parts and grew during heat treatment...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001808
EISBN: 978-1-62708-180-1
... grinding damage, machining marks or nicks, and quench cracks resulting from heat treating operations. Frequently, stress concentrators are introduced during hot or cold forming of shafts; these include surface discontinuities, such as laps, seams, pits and forging laps, and internal imperfections...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001022
EISBN: 978-1-62708-214-3
...Abstract Abstract Two complete aircraft undercarriage-leg 2014 aluminum alloy forgings and a number of sectional ends that exhibited cracks during nondestructive testing were examined to determine the extent of damage and the type of cracking. Cracks were primarily confined to the diaphragm...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003553
EISBN: 978-1-62708-180-1
.... As of 1972, the characteristics of SCC were known to include ( Ref 9 ): Tensile stress is required. This stress may be supplied by service loads, cold work, mismatch in fitup, heat treatment, and the wedging action of corrosion products. Only alloys are susceptible (no pure metals), although...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003510
EISBN: 978-1-62708-180-1
... Copper … 0.10 Prior Steel Structure The structure of the steel prior to hardening, for example, extruded, cast, forged, cold formed, and so on, may enhance the potential for cracking during the quench. Each as-formed structure requires a specific time and temperature cycle to condition...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001785
EISBN: 978-1-62708-241-9
... coalescence and rupture [ 3 ]. Although microvoids had formed, they were round and smooth rather than sharp edged. The round smooth fracture surface characteristic is due to insufficient bonding between two surfaces. Although not uncommon in cold welds, it is unusual in a forged component. On the basis...