1-10 of 10 Search Results for

UNS S34700

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c0091345
EISBN: 978-1-62708-220-4
.... Recommendations included replaced the material with type 304L stainless steel. Crater corrosion Heat exchanger tubes Nitric acid Welded joints 347 UNS S34700 Crevice corrosion Beveled weld-joint V-sections were fabricated to connect inlet and outlet sections of tubes in a type 347 stainless steel...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.aero.c0047590
EISBN: 978-1-62708-217-4
... induced by severe vibration in service. Additional tube clamps were provided to damp the critical vibrational stresses. No further fuel-line fractures were encountered. Engine components Heat affected zone Tubes Vibration 347 UNS S34700 Fatigue fracture Joining-related failures A weld in...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c0047753
EISBN: 978-1-62708-235-8
... and separation between braze and housing. Brazed joints Fatigue cracking Welding defects 347 UNS S34700 Fatigue fracture Joining-related failures A rectangular segment broke from the type 347 stainless steel housing of a pressure-probe assembly used in experimental instrumentation. The...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.process.c0089738
EISBN: 978-1-62708-235-8
... Undercutting Welded joints 347 UNS S34700 Fatigue fracture While undergoing vibration testing, a type 347 stainless steel inlet header for a fuel-to-air heat exchanger cracked in the header tube adjacent to the weld bead between the tube and header duct ( Fig. 1 ). Fig. 1 Type 347 stainless steel...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.modes.c9001705
EISBN: 978-1-62708-234-1
.... Coils (windings) Heat exchangers Lead Metal baths Wind tunnels 321 UNS S32100 347 UNS S34700 316 UNS S31600 Intergranular corrosion Intergranular fracture References 1. Midden R.E. , “Failure of CF 4 Heater Tubing After Cleaning to Remove Residual Lead...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001351
EISBN: 978-1-62708-215-0
... reactors Fast reactors Leakage Marine environments Nuclear reactor components, corrosion Pitting (corrosion) Welded joints, corrosion Weldments, corrosion 347 UNS S34700 Stress-corrosion cracking Selected Reference • Warke W. R. , Stress-Corrosion Cracking , Failure...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001056
EISBN: 978-1-62708-214-3
... circumferential length of the pipe without catastrophic failure. A thin stainless steel sleeve was inserted in the branch pipe to resolve the problem. Fracture mechanics Leakage Nuclear reactor components Piping Thermal fatigue 347 UNS S34700 Thermal fatigue fracture Selected...
Series: ASM Failure Analysis Case Histories
Volume: 3
Publisher: ASM International
Published: 01 December 2019
DOI: 10.31399/asm.fach.v03.c9001774
EISBN: 978-1-62708-241-9
... formation of polythionic acid in the process gas. ring type pipe joint fracture polythionic acid stainless steel transgranular fracture fractography creep strength 347 (austenitic wrought stainless steel) UNS S34700 321 (austenitic wrought stainless steel) UNS S32100...
Book Chapter

Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0003548
EISBN: 978-1-62708-180-1
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006783
EISBN: 978-1-62708-295-2