Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.mech.c0006900
EISBN: 978-1-62708-225-9
... behavior of type 316 stainless steel. The problem was solved by changing the clamp material from type 301 to type 316 stainless steel and by eliminating the MoS2 antiseize compound. Clamps, Materials Substitution Lubricants Sulfurization 301 UNS S30100 Brittle fracture Hydrogen damage and...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001360
EISBN: 978-1-62708-215-0
..., fatigue crack propagation, and final rapid fracture in a ductile manner The fatigue crack originated near a rivet hole. Automotive components Engine components Trucks 301 UNS S30100 Fatigue fracture Reference 1. Metals Handbook , 9th ed. , Vol. 9 , Metallography and...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001086
EISBN: 978-1-62708-214-3
... joints Weldments 301 UNS S30100 Intergranular fracture Intergranular corrosion Selected References • Forms of Corrosion , Failure Analysis and Prevention , Vol 11 , ASM Handbook , ASM International , 2002 , p 761 – 795 10.31399/asm.hb.v11.a0003548 • Lampman S...