... particle testing 1055 UNS G10550 Fatigue fracture A bridge wheel on a crane fractured after 1 year of service. The wheel was forged from 1055 steel. The wheel fractured in the web between the hub and the rim. Investigation Visual examination of the fracture surface revealed a small area...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.matlhand.c0048102
EISBN: 978-1-62708-224-2
... the web surface. Fatigue cracking of the wheel was initiated at forging defects in the web. Replacement wheels were machined all over and were magnetic particle inspected to detect any cracks that could act as stress raisers. Cracks Defects Magnetic particle testing 1055 UNS G10550 Fatigue...