The origins of the casting are unknown. It is included here as a classic case of intergranular corrosion. The part (apparently a pump outlet) was named the “rubber casting” because of the severity of the intergranular attack. Every grain boundary has been attacked to the extent that the casting could be twisted and stretched as through made of rubber. The chemistry of the casting was acceptable for CN-7M. The reason the part failed is a continuous film of carbide with a continuous crack running parallel to the carbides. This sensitized structure produces an area depleted in protective chromium, making it susceptible to corrosion. Two solutions to this problem are available. The simplest is to ensure correct heat treatment to dissolve grain-boundary carbide film and return the protective chromium to the depleted zone. Alternatively, a low-carbon (0.03% maximum C, for example, CF-3) grade can be specified. Procedures are given in a reference for screening castings that may be susceptible to intergranular corrosion due to processing errors.

The information provided in this article is intended for those individuals who want to determine why a casting component failed to perform its intended purpose. It is also intended to provide insights for potential casting applications so that the likelihood of failure to perform the intended function is decreased. The article addresses factors that may cause failures in castings for each metal type, starting with gray iron and progressing to ductile iron, steel, aluminum, and copper-base alloys. It describes the general root causes of failure attributed to the casting material, production method, and/or design. The article also addresses conditions related to the casting process but not specific to any metal group, including misruns, pour shorts, broken cores, and foundry expertise. The discussion in each casting metal group includes factors concerning defects that can occur specific to the metal group and progress from melting to solidification, casting processing, and finally how the removal of the mold material can affect performance.

This article focuses on the general root causes of failure attributed to the casting process, casting material, and design with examples. The casting processes discussed include gravity die casting, pressure die casting, semisolid casting, squeeze casting, and centrifugal casting. Cast iron, gray cast iron, malleable irons, ductile iron, low-alloy steel castings, austenitic steels, corrosion-resistant castings, and cast aluminum alloys are the materials discussed. The article describes the general types of discontinuities or imperfections for traditional casting with sand molds. It presents the international classification of common casting defects in a tabular form.