Published: 01 June 2019
Fig. 1 Cracks in pressure vessel made of ASTM A515 carbon steel lined with type 405 stainless steel. Failure occurred at plug welds because of dilution of weld metal. (a) Micrograph of specimen through weld area etched in acid cupric chloride showing ASTM A515 carbon steel (top), interface More
Image
Published: 30 August 2021
Fig. 29 Cracks in pressure vessel made of ASTM A515 carbon steel lined with type 405 stainless steel. Failure occurred at plug welds because of dilution of weld metal. (a) Micrograph of specimen through weld area etched in acid cupric chloride showing ASTM A515 carbon steel (top), interface More
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.petrol.c0048808
EISBN: 978-1-62708-228-0
... Abstract The welds joining the liner and shell of a fluid catalytic cracking unit failed. The shell was made of ASTM A515 carbon steel welded with E7018 filler metal. The liner was made of type 405 stainless steel and was plug welded to the shell using ER309 and ER310 stainless steel filler...
Series: ASM Failure Analysis Case Histories
Volume: 1
Publisher: ASM International
Published: 01 December 1992
DOI: 10.31399/asm.fach.v01.c9001053
EISBN: 978-1-62708-214-3
... Abstract A carbon steel (ASTM A515 grade 70) pressure vessel failed by brittle fracture while being hydro tested in the fabricating shop. The fracture origin was a small crack at a welding arc strike associated with the toe of a nozzle weld. A fracture mechanics calculation indicated...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.power.c0048777
EISBN: 978-1-62708-229-7
... Abstract A 150 cm ID boiler drum made form ASTM A515, grade 70, steel failed during final hydrotesting at a pressure of approximately 26 MPa. Brittle fractures were revealed in between two SA-106C nozzles and remainder was found to involve tearing. Short, flat segments of fracture area...
Series: ASM Handbook Archive
Volume: 11
Publisher: ASM International
Published: 01 January 2002
DOI: 10.31399/asm.hb.v11.a0001818
EISBN: 978-1-62708-180-1
... Hydrotesting A 150-cm (60-in.) inside-diameter boiler drum fabricated of 18-cm (7-in.) thick ASTM A515, grade 70, steel failed during final hydrotesting at a pressure of approximately 26 MPa (3.8 ksi). The shock wave from the vessel rupture also damaged several connected headers and piping runs...
Series: ASM Handbook
Volume: 11
Publisher: ASM International
Published: 15 January 2021
DOI: 10.31399/asm.hb.v11.a0006759
EISBN: 978-1-62708-295-2
... 2009 3. “ Standard Specification for Carbon Structural Steel,” A36/A36M-14 , ASTM 4. “ Standard Specification for High-Strength Low-Alloy Columbian-Vanadium Structural Steel ,” A572 – A515 , ASTM 5. “ Standard Guide for Quantitative Analysis by Energy Dispersive Spectroscopy ,” E1508...
Series: ASM Handbook
Volume: 11A
Publisher: ASM International
Published: 30 August 2021
DOI: 10.31399/asm.hb.v11A.a0006812
EISBN: 978-1-62708-329-4
... diameter boiler drum fabricated of 18 cm (7 in.) thick ASTM A515, grade 70 steel plate failed during final hydrotesting at a pressure of approximately 26 MPa (3.8 ksi). The shock wave from the vessel rupture also damaged several connected headers and piping runs. A schematic of the crack path, including...