1-3 of 3 Search Results for

ASME SA106 B

Follow your search
Access your saved searches in your account

Would you like to receive an alert when new items match your search?
Close Modal
Sort by
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001327
EISBN: 978-1-62708-215-0
... Abstract Three ASME SA106 grade B carbon steel feed water piping reducers from a pressurized water reactor showed indications of flaws near welds during ultrasonic testing. Further examination and testing indicated that the cracks resulted from a low-cycle corrosion fatigue phenomenon...
Series: ASM Failure Analysis Case Histories
Volume: 2
Publisher: ASM International
Published: 01 December 1993
DOI: 10.31399/asm.fach.v02.c9001323
EISBN: 978-1-62708-215-0
... hydroxide, environment UNS S31600 316 ASME SA106 B Stress-corrosion cracking U-bend T2 was a replacement bend made out of two 90° elbows. U-bends T3 and T4 were original to the boiler. U-bend T3 contained a patch weld over a past failure. Both tubes 1T and 4T had been...
Series: ASM Failure Analysis Case Histories
Publisher: ASM International
Published: 01 June 2019
DOI: 10.31399/asm.fach.chem.c9001686
EISBN: 978-1-62708-220-4
... of failure was low flow transient operation. Coils (windings) Electric power generation Vaporizers ASME SA106 B Transgranular fracture Thermal fatigue fracture A metallurgical failure analysis was performed on a failed vaporizer coil removed from a horizontal forced...