An automatic press for making burlap bags had been used for several years. The press failed after being shipped by truck for a distance of about 400 mi. The objective was to determine whether failure occurred during or before shipment. The large piece which broke off the press included a section of the ways and a heavy adjustable mechanism which normally rides on these ways. The weight of the broken section was estimated at several hundred pounds. There was no support for the broken piece beyond the point of breakage. The material was a commercial cast iron, and the largest proportion of the fracture area was fresh and bright. It was concluded that this was a fresh fracture which occurred during shipment, and the crack itself was not present prior to shipment. The fact that a material defect of some sort was present and probably determined the location of the crack was apparently not significant as far as its usage was concerned. The failure could have been avoided by providing support underneath the overhanging member.

Fundamentals of fatigue failure are outlined. Addressed are fatigue crack characteristics, basic crack types, unidirectional bending, alternate bending, rotary bending, torsion, direct stress, and combined stress. Stress cycle, endurance limits, under and overstressing, stress concentration, and surface condition are discussed. Sections are devoted to fatigue crack assessment, corrosion relation to fatigue failure, and the micro-mechanisms of fatigue failure. Materials considered include steels. Photographs of service failures are used to illustrate features alluded to in the text.

This article focuses on the mechanisms of microbially induced or influenced corrosion (MIC) of metallic materials as an introduction to the recognition, management, and prevention of microbiological corrosion failures in piping, tanks, heat exchangers, and cooling towers. It discusses the degradation of various protective systems, such as corrosion inhibitors and lubricants. The article describes the failure analysis of steel, iron, copper, aluminum, and their alloys. It also discusses the probes available to monitor conditions relevant to MIC in industrial systems and the sampling and analysis of conditions usually achieved by the installation of removable coupons in the target system. The article also explains the prevention and control strategies of MIC in industrial systems.