A stamped coin exhibited visible discolored areas, seen as a tan haze on the surface. The discoloration was considered merely cosmetic. The nonstained and stained regions were studied using SEM/EDS. Greater amounts of aluminum and magnesium were found in the stained area as compared with the nonstained region. Some carbon and oxygen were detected in both areas, which may be suggestive of organic substances. Fourier transform infrared spectroscopy (FTIR) revealed traces of hydrocarbons and ether/alcohol materials in the stained area, suggesting that the stain was associated with a cellulose or carbohydrates (sugars). These findings, along with the appearance, suggest that a sugar-containing substance, such as coffee or a soft drink, dried onto the surface of this coin and caused the observed discoloration.

The paper discusses the analysis of a coating defect on a high phosphorus electroless nickel (Ni-11 wt. % P) deposit plated on an aluminum alloy substrate. Preliminary investigations had indicated that the elongated defects were possibly caused by the entrapment of long fibers or particles during the plating. The possible sources of fibers were identified. The SEM/EDS analysis of fibers collected from the air duct filters correlated very well with the defect shape and the EDS profile collected from under the defect site. It appears that the fibers from air duct filters directly above the plating line were blown into the plating tank and getting co-deposited. The paper describes the step-by-step analysis of the defect that led to successful identification of the root cause of the defect.