An Inconel-clad SA-212 Grade B carbon steel inlet cone with an anticipated 25-year service life failed in a localized area after only seven years of service. The failure was caused by an erosion/corrosion leak at the midsection. Erosion/corrosion was confined to a localized area directly facing the steam inlet nozzle. The Inconel cladding was intact elsewhere in the inlet cone with insignificant corrosion-related degradation. In the absence of the conditions that led to erosion/corrosion, the Inconel clad carbon steel was considered adequate for the intended service. As a corrective measure, a solid Inconel liner was recommended in the areas of direct steam impingement.

The Pandia digester is a long cylindrical vessel which uses alkaline sulfite liquor to cook sawdust for pulping. The inlet cone was fabricated from AISI 304L stainless steel with E308 welds. Typical liquor concentration was approximately 80% NaOH, 20% Na2SO3 with chloride concentrations at 2 grams per liter. The operating pressures in the inlet cone were up to 1.2 MN/sq m (170 psig). The inlet cone had developed leaks within a year of service. Liquid penetrant inspection showed significant through-wall cracking near the fillet welds joining the bottom flange and side wall and the butt welds. Metallographic specimens were prepared from the welds to examine the microstructure and nature of the cracks. The cooking liquor at the inlet cone contained over ppm chlorides and was aggressive to 304 stainless steel. The cracking was identified as chloride-induced SCC. The inlet cone was replaced with an Inconel clad carbon steel inlet cone to combat the SCC.