A type 431 stainless steel mushroom-head closure fractured in service at a hydrogen pressure of 3000 atm. Fracture occurred at room temperature after miscellaneous chemical service that included exposures to hydrogen at temperatures from ambient to 350 deg C (662 deg F). Investigation (visual inspection and 2400x/6600x TEM analysis) supported the conclusion that failure was caused by hydrogen embrittlement, not SCC as might have been suspected. No recommendations were made.

A steel pot used as crucible in a magnesium alloy foundry developed a leak that resulted in a fire and caused extensive damage. Hypotheses as to the cause of the leak included a defect in the pot, overuse, overheating, and poor foundry practices. Scanning electron microscopy, transmission electron microscopy, optical microscopy, and x-ray microanalysis in conjunction with dimensional analysis, phase diagrams and thermodynamics considerations were employed to evaluate the various hypotheses. All evidence pointed to an oxide mass in the area where the hole developed, likely introduced during the steelmaking process.