An AISI type 303(Se) stainless steel eye terminal that was roll swaged on the end of a 9.5 mm diam wire rope cracked extensively after one year of service. A hairline crack that had initiated at the inner surface of the fitting was revealed by metallographic examination of a sectioned terminal specimen. It was indicated by the holes in the region adjoining the crack and rough texture of the crack surface that a corrosive medium (presumably seawater) had entered the crack from the inner surface of the fitting and coupled with the hairline crack to develop crevice corrosion. The crack propagated toward the outer surface due to high residual stresses in the swaged metal and was followed closely by corrosion. Stress corrosion as result of a combination of residual stresses plus load stress and corrosion was found to cause the failure. Rotary swaging or swaging in a punch press was recommended instead of roll swaging as they made deformation more symmetrical.

Two sections of a galvanized cable 10.5 A 160 GR +NORM M 9533 (round stranded cable of normal type, h + 6, Langslay, right-handed) were examined. One had a 100 mm long blackish-brown tarnished zone obviously caused by localized heating at one end, inside which the hemp core was missing, and the other corresponded to the original condition of the cable. The cause of the damage was unknown. About a third of the wires had fractured and the rest had been cut. All were tensile fractures with a relatively high degree of necking. The cause of the localized heating was unknown. It can only be concluded from the investigation that the temperature did not exceed the Ac3 point of the wire material, which should be about 750 deg C, and that the heating lasted a fairly long time.

Initially, two vertical double-acting two-stage compressors delivering chlorine gas at a pressure of 100 psi appeared to be running satisfactorily. About six months later the LP piston-rod of the No. 2 compressor failed due to burning, the compressor being worked double-acting at the time. About five months later, the HP piston rod of the No. 1 compressor failed in a similar manner. Specimens for microscopic examination were cut from the rod in the region of the failure and from the extreme end that had been situated above the piston and hence not subjected to an appreciable rise in temperature. The material was a steel in the normalized condition with a 0.35% C content. It appears probable that deficient lubrication of the gland resulted in overheating of the rod due to friction. The presence of a sprayed-metal coating was probably an additional factor in promoting failure, as it would present to the gas a surface area considerably greater than that of a homogeneous material.

An electronic sensor coil failed continuity testing, indicating that a break was present in the polymer-coated wire. An area of the wire showed a green discoloration and the break in the wire was located in this same region. The discoloration was suspected to be an indicator of what caused the failure. SEM/EDS and FTIR results showed the break in the coil wire was associated with corrosion. The corrosion debris contained relatively high levels of sodium and chlorine, which were likely in the form of salt. Some salt deposits were noted also in other areas along the wire surface. The findings suggested salt or salt water had leaked into the sensor and caused localized corrosion to the wire, possibly at an area where preexisting damage was present in the coating. Separation occurred in the wire when the current density at the reduced cross section caused excessive localized heating, which led to melting of the wire.

The connecting end of two forged medium-carbon steel rods used in an application in which they were subjected to severe low-frequency loading failed in service. The fractures extended completely through the connecting end. The surface hardness of the rods was found to be lower than specifications. The fractures were revealed to be in areas of the transition regions that had been rough ground to remove flash along the parting line. The presence of beach marks, indicating fatigue failure, was revealed by examination. The fracture origin was confirmed by the location and curvature of beach marks to be the rough ground surface. An incipient crack 9.5 mm along with several other cracks on one of the fractured rods was revealed by liquid penetration examination. Metallographic examination of the fractured rods indicated a banded structure consisting of zones of ferrite and pearlite. It was established that the incipient cracks found in liquid-penetrant inspection had originated at the surface in the banded region, in areas of ferrite where this constituent had been visibly deformed by grinding. Closer control on the microstructure, hardness of the forgings and smooth finish in critical area was recommended.

A drawing plant which processed steel wire of designation 105 Cr 2 for ball bearings had losses due to crack formation and wire breakage during drawing. To establish the reason for the breakage, seven fractures were submitted for investigation with contiguous wire segments on both sides of the fracture of 300 mm each. Missing in the lamellar surface structure, with the exception of the remnants of a coarse network, were the pre-eutectically precipitated carbides to be expected in this steel. Surrounding the ferritic region in the surface structure, a ring of lamellar pearlite is seen, which turns into the granular annealed structure towards the core. The described structural phenomena were noted in all of the seven fracture regions. Their intensity always decreased with increasing distance from the fracture. Surface decarburization caused the formation of lamellar pearlite during annealing. This investigation further revealed that the localized decarburization and pearlite formation was present already in the rolled wire in uneven distribution over the entire coil length.

Cold-drawn type 303 stainless steel wire sections, 6.4 mm (0.25 in.) in diameter, failed during a forming operation. All of the wires failed at a gradual 90 deg bend. Investigation (visual inspection and 5.3x/71x/1187x SEM views) supported the conclusion that the wires cracked due to ductile overload. The forming stresses were sufficient to initiate surface ruptures, suggestive of having exceeded the forming limit. Recommendations included examining the forming process, including lubrication and workpiece fixturing.

Banding wires of the rotor of an 1800 hp motor were renewed following replacement of the banding rings. After about six months of service, a breakdown occurred due to bursting of the banding wires in several places. The 0.064 in. diam wire was nonmagnetic and of the 18/8 Cr-Ni type of austenitic stainless steel. The fractures were short and partially crystalline, with no evidence of slowly developing cracks of the fatigue type. Microscopical examination of sections taken through the fractures showed the cracking to be of the multiple branching type. Because the material was in the heavily cold-worked condition, it was not possible to determine with certainty if the cracks were of the inter- or trans-granular type. It was concluded that failure was due to stress-corrosion cracking in a chloride environment. Failure of the wires was likely due to the use of a chloride-containing flux during the soldering operation.

A bolt manufacturer observed that products made from certain shipments of steel 41 Cr4 wire were prone to the formation of quench cracks in their rolled threads. The affected wire was tested and found to be highly sensitive to overheating because of the metallurgical method by which it was produced. A stronger decarburization of the case was a contributing factor that could not be prevented by working because the thread was rolled. Hardening tests conducted by the bolt manufacturer showed that quench cracks did not occur in specimens that were turned down before hardening and when notches were machined instead of beaten with a chisel.

A 2.3 mm diam steel wire broke during cable twisting. The fracture occurred obliquely to the longitudinal axis of the wire and showed a constriction at the end. Therefore it was a ductile fracture. File mark type work defects were noticeable on the wire surface at both sides of the fracture, but they had no effect on the breakage of the wire. Away from the fracture area, the wire had a normal structure of hyperfine lamellar pearlite (sorbite) of a “patented” and cold drawn steel wire. In the vicinity of the fracture, the cementite of the pearlite was partially spheroidized, while at the fracture itself it was completely spheroidized. Therefore the wire was locally annealed at this point. It was likely that the wire cracked at this point during the last drawing and then broke during twisting due to its lower strength in the weakened cross section after prior deformation.

An articulated rod (made from 4337 steel (AMS 6412) forging, quenched and tempered to 36 to 40 HRC) used in an overhauled aircraft engine was fractured after being in operation for 138 h. Visual examination revealed that the rod was broken into two pieces 6.4 cm from the center of the piston-pin-bushing bore. The fracture was nucleated at an electroetched numeral 5 on one of the flange surfaces. A notch, caused by arc erosion during electroetching, was revealed by metallographic examination of a polished-and-etched section through the fracture origin. A remelted zone and a layer of untempered martensite constituted the microstructure of the metal at the origin. Small cracks, caused by the high temperatures developed during electro-etching, were observed in the remelted area. It was concluded that fatigue fracture of the rod was caused by the notch resulting from electroetching and thus electroetched marking of the articulated rods was discontinued as a corrective measure.

The small cable (drop wire) providing service for individual subscribers from the aerial plant is held in place by a clamp made of a tin-coated brass body (attached to the cable) and a copper tail wire loop (attached to a galvanized steel hook or to a porcelain insulator). The tail wire is 2.6 mm (0.102 in.) diam annealed copper, and the clamp assembly must withstand a 2470 N (555 lb) load without breaking or slipping. A number of these clamps, located a few hundred feet from the ocean, have failed. The sharply broken wire indicated to weakening by abrasion. The copper tail wire failures had characteristics generally associated with corrosion fatigue. The broken wires showed multiple transgranular cracks near the failure, originating at the bases of pits. It was diagnosed that the copper tail wire failures were due to corrosion fatigue. The solution to this problem was to change the tail wire material for direct seashore exposure from annealed copper to annealed Monel.

An electron probe microanalyzer was applied to the study of service failures (due to severe heating) of aluminum wire connections in residential electrical circuits. Perturbed regions in which the composition underwent a change during the failure were revealed by optical and scanning electron microscopy of the contacts. A sequence of iron-aluminum compositions that shift from the pure aluminum of the wire to the nearly pure iron of the screw was revealed by analyses of two distinct layers formed on the aluminum/iron region. The compositions were found to correspond to specific intermetallic compounds found in the aluminum-iron phase diagram. Similar compositional variations were noted at the aluminum/brass interface. It was concluded that the failure of the electrical junction due to extreme heating was related to the formation of intermetallic compounds at the current carrying interfaces. These intermetallics were established to have a high resistance causing significant resistive heating.

Drive cables from a rubber processing machine were failing in less than 8 h of operation, the expected service life being much greater than 100 h. Comparison cables were tested to failure under known stress conditions, including tensile overload, torsional loading, reversed bending alternating stress, and buckling (compressive) cyclic loading. The mode of failure was found to be reversed bending fatigue caused by drive cables moving over guide pulleys of small radii. Modifications of the machinery and drive cable system were suggested.

This article focuses on the mechanisms and common causes of failure of metal components in lifting equipment in the following three categories: cranes and bridges, particularly those for outdoor and other low-temperature service; attachments used for direct lifting, such as hooks, chains, wire rope, slings, beams, bales, and trunnions; and built-in members such as shafts, gears, and drums.

Over a period of 2 or 3 years, 40 to 50 premature failures of drawn high-tensile, pearlitic high-carbon (0.8 wt% C) steel wires used as cables for towing targets behind aircraft occurred. Six service failures were examined in detail. Four types of failure characteristics were noted. A close examination of wire that had been flown several times without failure was also made, and dynamic tests were conducted to investigate the fracture characteristics of wire subjected to dynamic loading. It was concluded that dynamic shock loading transmitted by the target during unsteady flight conditions was the major cause of failure. Recommendations emphasized the need for a suitable shock absorber to be fitted at the constant-tensioning device of the winch system.