Fracture of a Mild Steel Crane Hook
-
Published:2019
Abstract
A crane hook was stamped S.W.L. 3 tons and, while its main dimensions were in approximate accordance with those specified in B.S. 482 for a hook of this capacity, its shape in some respects was not exactly in conformity with that recommended. At the time of fracture, the load being lifted was slightly under 10 cwts. Fracture occurred away from the normal wearing surface where the hook makes contact with the lifting slings. There was no evidence that fracture was preceded by any appreciable deformation locally or in the region of the failure. A sulphur print, taken on a cross section of the hook adjacent to the plane of fracture, showed the hook was made from a killed steel free from major segregation. Microscopic examination showed the material to be a mild steel in the normalized condition, the carbon content being of the order of 0.25%. Bend tests showed the material at the intrados of the hook would deform in a ductile manner both under slow and impact-loading conditions if in the form of an unnotched test piece, but if notched, it failed in a brittle manner under impact, though not under slow loading.
Fracture of a Mild Steel Crane Hook, ASM Failure Analysis Case Histories: Construction, Mining, and Agricultural Equipment, ASM International, 2019, https://doi.org/10.31399/asm.fach.conag.c9001471
Download citation file:
New Handbook: Volume 11B
Now available in the Digital Library! Volume 11B serves as a reference and guide to help engineers determine the causes of failure in plastic components and make corrective adjustments through design and manufacturing modifications.