Near-surface porosity in zinc die castings that were subsequently plated with copper, nickel, and bright chromium was causing blemishes in the plating. Identifying die casting turbulence and hot spots were keys to process modifications that subsequently allowed porosity to be greatly minimized.
You do not currently have access to this chapter.
Citation
D. Aliya, Plating Blemishes in Zinc Die Castings, ASM Failure Analysis Case Histories: Processing Errors and Defects, ASM International, 2019, https://doi.org/10.31399/asm.fach.process.c9001641
Download citation file:
Oct. 28 – Nov. 1 | San Diego
Keep up-to-date at the premier event for the microelectronics failure analysis community. Register today for ISTFA 2024!
Related Book Content
Metal Waves or Laking on Zinc-Based Diecastings
ASM Failure Analysis Case Histories: Processing Errors and Defects
Broken Full Lift Disk of a Safety Valve
ASM Failure Analysis Case Histories: Mechanical and Machine Components
Coolant Leakage Through a Cylinder-Head Exhaust Port Caused by Shrinkage Porosity
ASM Failure Analysis Case Histories: Automobiles and Trucks
Failure of Steel Jaws
ASM Failure Analysis Case Histories: Machine Tools and Manufacturing Equipment
Tensile Fracture That Originated at Shrinkage Porosity in a Cast Low-Alloy Steel Connector
ASM Failure Analysis Case Histories: Buildings, Bridges, and Infrastructure
Failure of Die Cast Aluminum Cluster Bomb Tailcone Assemblies
ASM Failure Analysis Case Histories: Processing Errors and Defects
Fractured Swivel Head
ASM Failure Analysis Case Histories: Steelmaking and Thermal Processing Equipment
Failure of a Yoke Body of Master Slave Manipulator Due to Casting Defect
Handbook of Case Histories in Failure Analysis
Failure of Compound Bow Handle Risers
Handbook of Case Histories in Failure Analysis
Cracks in Cylinder Blocks and in Cast Iron Cylinder Head
ASM Failure Analysis Case Histories: Construction, Mining, and Agricultural Equipment