Failure of a Nickel-Base Alloy Incinerator Liner
-
Published:2019
Search within book:
Abstract
An alloy IN-690 (N06690) incinerator liner approximately 0.8 mm (0.031 in.) thick failed after only 250 h of service burning solid waste. Investigation supported the conclusion that the root cause of the failure was overfiring during startup and sulfidation of the nickel-base alloy. No recommendations were made.
You do not currently have access to this chapter.
Sign in
Don't already have an account? Register
You could not be signed in. Please check your email address / username and password and try again.
ASM members
Member Sign InCitation
Failure of a Nickel-Base Alloy Incinerator Liner, ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions, ASM International, 2019, https://doi.org/10.31399/asm.fach.usage.c0091756
Download citation file:
Join Failure Analysis Society
The ASM Failure Analysis Society (FAS) is a community where failure analysis professionals from all over the world can learn and grow in their field
Related Book Content
Failure Analysis of a Pilot Scale Melter
ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions
Perforation of a Nickel-Base Alloy Kiln
ASM Failure Analysis Case Histories: Steelmaking and Thermal Processing Equipment
Oxidized Recuperator Pipes
ASM Failure Analysis Case Histories: Steelmaking and Thermal Processing Equipment
Failure of a Heat-Resistant Sinter Belt
Handbook of Case Histories in Failure Analysis
Pitting of a Condenser Tube in a Saltwater Heat Exchanger Due to Hydrogen Sulfide Contamination
ASM Failure Analysis Case Histories: Chemical Processing Equipment
Corrosion Failure of a Tee Fitting
ASM Failure Analysis Case Histories: Oil and Gas Production Equipment
Hydrogen-Stress Cracking of Type 410 Stainless Steel Splice Case Bolts
ASM Failure Analysis Case Histories: Mechanical and Machine Components
Hydrogen-Stress Cracking of Type 301 Stainless Steel Clamp
ASM Failure Analysis Case Histories: Mechanical and Machine Components
Hot Corrosion of Stage 1 Nozzles in an Industrial Gas Turbine
Handbook of Case Histories in Failure Analysis
Pitting Corrosion of Steel Tubes in an Air Preheater
ASM Failure Analysis Case Histories: Power Generating Equipment