Eddy Current Inspection of Pitting and Stress-Corrosion Cracking of Type 316 Stainless Steel Evaporator Tubes in a Chemical Processing Operation
-
Published:2019
Abstract
Eddy current inspection was performed on a vertical evaporator unit (that contained 180 tubes) used in a chemical processing plant. It was advised that the tube material was type 316 stainless steel. The shell-side fluid was condensate and gaseous methylene chloride, while the tube-side fluid was contaminated liquid methylene chloride. More than 100 tubes exhibiting severe outer surface pitting and cracklike indications near each tube sheet were revealed during eddy current inspection. It was observed that the indications correlated with rust-stained, pitted, and cracked areas on the outer surfaces. The cracking was revealed by metallographic examination to have initiated...
Sign in
ASM members
Member Sign InEddy Current Inspection of Pitting and Stress-Corrosion Cracking of Type 316 Stainless Steel Evaporator Tubes in a Chemical Processing Operation, ASM Failure Analysis Case Histories: Chemical Processing Equipment, ASM International, 2019, https://doi.org/10.31399/asm.fach.chem.c0060104
Download citation file:
Join Failure Analysis Society
The ASM Failure Analysis Society (FAS) is a community where failure analysis professionals from all over the world can learn and grow in their field.