Failures of Forged End Bells on Large Electric Generators
-
Published:2019
Abstract
Forged austenitic steel rings used on rotor shafts in two 100,000 kW generators burst from overstressing in a region of ventilation holes. A variety of causes contributed to the brittle fractures in the ductile austenitic alloy, including stress concentration by holes, work hardened metal in the bores, and a variable pattern of residual stress.
You do not currently have access to this chapter.
Sign in
Don't already have an account? Register
You could not be signed in. Please check your email address / username and password and try again.
ASM members
Member Sign InCitation
Failures of Forged End Bells on Large Electric Generators, ASM Failure Analysis Case Histories: Failure Modes and Mechanisms, ASM International, 2019, https://doi.org/10.31399/asm.fach.modes.c9001724
Download citation file:
Join Failure Analysis Society
The ASM Failure Analysis Society (FAS) is a community where failure analysis professionals from all over the world can learn and grow in their field.
Related Book Content
Another Turbogenerator Failure
ASM Failure Analysis Case Histories: Power Generating Equipment
Brittle Fracture of a Cadmium-Plated 4140 Steel Retaining Ring at a Hard Spot Caused by an Arc Strike
ASM Failure Analysis Case Histories: Mechanical and Machine Components
Brittle Fracture of Rocket-Motor Case That Originated at Delayed Quench Cracks
ASM Failure Analysis Case Histories: Processing Errors and Defects
Brittle Fracture of a Roll-Assembly Sleeve Due to Improper Microstructure
ASM Failure Analysis Case Histories: Failure Modes and Mechanisms
Fracture of 99.90 Pure Tin Tubes
ASM Failure Analysis Case Histories: Chemical Processing Equipment
Cemented Carbides: Atlas of Fractographs
Fractography
Fracture of an Accumulator Ring Due to Hydrogen Embrittlement
ASM Failure Analysis Case Histories: Processing Errors and Defects
Condition Assessment and Improvement of a Steam Turbine Rotor
Handbook of Case Histories in Failure Analysis
Failure of a Reversible Flap Valve in a Thermal Power Station
Handbook of Case Histories in Failure Analysis
Failure of a Jack Cylinder
ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions