Wear Failure of an Antifriction Bearing
-
Published:2019
Abstract
An antifriction bearing made from a nylon/ polyethylene blend failed. The bearing came into contact with a steel shaft. Investigation (visual inspection and 417X images) supported the conclusion that movement of the shaft against the bearing caused abrasion due to fine iron oxide particles. No recommendations were made.
You do not currently have access to this chapter.
Citation
Wear Failure of an Antifriction Bearing, ASM Failure Analysis Case Histories: Failure Modes and Mechanisms, ASM International, 2019, https://doi.org/10.31399/asm.fach.modes.c0092101
Download citation file:
Oct. 28 – Nov. 1 | San Diego
Keep up-to-date at the premier event for the microelectronics failure analysis community. Register today for ISTFA 2024!
Related Book Content
Friction and Wear of Rolling-Element Bearings
Friction, Lubrication, and Wear Technology
Abrasive Wear Failures
Failure Analysis and Prevention (2021 Edition)
Wear Failures—Abrasive and Adhesive
Understanding How Components Fail (Third Edition)
Wear Failure of Reinforced Polymers
Characterization and Failure Analysis of Plastics
Catastrophic Failure of a Hoist Worm Caused by Destructive Wear Resulting From Abusive Operation
ASM Failure Analysis Case Histories: Improper Maintenance, Repair, and Operating Conditions
Grinding Plate Wear Failure Analysis
ASM Failure Analysis Case Histories: Machine Tools and Manufacturing Equipment
Wear Failure of a Fuel-Pump Drive Shaft Caused by the Presence of Sand, Metallic Particles, and Vibration
ASM Failure Analysis Case Histories: Air and Spacecraft
Wear Failures of Reinforced Polymers
Characterization and Failure Analysis of Plastics
Microstructural Manifestations of Fractured Z-Profile Steel Wires on the Outer Layer of a Failed Locked Coil Wire Rope
ASM Failure Analysis Case Histories: Buildings, Bridges, and Infrastructure
Failure of a Hard-Faced Stainless Steel Pump Sleeve Because of Abrasive Wear by River-Water Silt
ASM Failure Analysis Case Histories: Failure Modes and Mechanisms