Landing Gear and Undercarriage Components
-
Published:2019
Abstract
One main undercarriage axle made of high strength alloy steel was subjected to simulated fatigue test for 6000 h of service. After only 300 h it broke in two along the sharp radius. The fracture revealed a coarse, irregular, and brittle surface before final fracture by thick angular shear lip zone. The presence of micropores in the cleavage facets as well as at the grain boundaries and hairline type crack indications under SEM examination were all suggestive of hydrogen embrittlement. On the basis of investigation results and observations, it was concluded that the transverse breakage of the axle had occurred intergranularly in a brittle manner, possibly, initiated by a shallow zone of fatigue along the sharp radius acting as stress riser.
Landing Gear and Undercarriage Components, ASM Failure Analysis Case Histories: Air and Spacecraft, ASM International, 2019
Download citation file:
Oct. 28 – Nov. 1 | San Diego
Keep up-to-date at the premier event for the microelectronics failure analysis community. Register today for ISTFA 2024!