Fatigue Cracking of Two Crankshafts Due to Welding
-
Published:2019
Abstract
Two diesel engine crankshafts of similar dimensions, the journal diam being approximately 7 in., failed due to cracking originating in the fillet at the junction between the crankpin and the web nearest to the flywheel. The cracks were discovered before rupture occurred. Several small cracks originated in the fillet, ran together and developed as two main crack fronts that ultimately merged into one, a typical example of a fatigue failure. Electromagnetic crack detection revealed the presence of a number of discontinuities which were located at a position that would correspond to the vertical axis of the original ingot. The crankshaft had not been stress-relieved after a welding operation had been carried out. The only satisfactory course to follow when dealing with a highly stressed part in which defects of the type in question are revealed during machining is to scrap the forging.
Fatigue Cracking of Two Crankshafts Due to Welding, ASM Failure Analysis Case Histories: Offshore, Shipbuilding, and Marine Equipment, ASM International, 2019, https://doi.org/10.31399/asm.fach.marine.c9001429
Download citation file:
Oct. 28 – Nov. 1 | San Diego
Keep up-to-date at the premier event for the microelectronics failure analysis community. Register today for ISTFA 2024!