Cracking in a Reducing Pipe From a Pressurized Water Reactor
By
Carl J. Czajkowski
Carl J. Czajkowski
Department of Nuclear Energy, Brookhaven National Laboratory
Search for other works by this author on:
-
Published:1993
Page range:
163 - 167
Abstract
Three ASME SA106 grade B carbon steel feed water piping reducers from a pressurized water reactor showed indications of flaws near welds during ultrasonic testing. Further examination and testing indicated that the cracks resulted from a low-cycle corrosion fatigue phenomenon.
You do not currently have access to this chapter.
Citation
Carl J. Czajkowski, Cracking in a Reducing Pipe From a Pressurized Water Reactor, Handbook of Case Histories in Failure Analysis, Vol 2, Edited By Khlefa A. Esaklul, ASM International, 1993, p 163–167, https://doi.org/10.31399/asm.fach.v02.c9001327
Download citation file:
Join Failure Analysis Society
The ASM Failure Analysis Society (FAS) is a community where failure analysis professionals from all over the world can learn and grow in their field.
Related Book Content
Corrosion Fatigue Cracking of a Steam Generator Vessel From a Pressurized Water Reactor
Handbook of Case Histories in Failure Analysis
Corrosion Failure of Stainless Steel Components During Surface Pretreatment
Handbook of Case Histories in Failure Analysis
Corrosion Failure of a Tee Fitting
ASM Failure Analysis Case Histories: Oil and Gas Production Equipment
Failure of an Aluminum Brass Condenser Tube
Handbook of Case Histories in Failure Analysis
Role of Powder Metallurgy Industries in Various Sectors―Part 1
Powder Metallurgy and Additive Manufacturing: Fundamentals and Advancements
Stress-Corrosion Cracking of Alloy X-750 Jet Pump Beams
ASM Failure Analysis Case Histories: Power Generating Equipment
Failure of a Brass Pipe Nipple
Handbook of Case Histories in Failure Analysis
Environmentally Assisted Cracking
Corrosion of Aluminum and Aluminum Alloys
Inspection and Evaluation of Weldments
Weld Integrity and Performance
Advantages of Steel Castings
Steel Castings Handbook (Sixth Edition)